The interest in nanoscale materials stems from the fact that new properties are acquired at this length scale and, equally important, that these properties * To whom correspondence should be addressed. Phone, 404-8940292; fax, 404-894-0294; e-mail, mostafa.el-sayed@ chemistry.gatech.edu. † Case Western Reserve UniversitysMillis 2258. ‡ Phone, 216-368-5918; fax, 216-368-3006; e-mail, burda@case.edu. § Georgia Institute of Technology. 1025 Chem. Rev. 2005, 105, 1025−1102

Chemistry and properties of nanocrystals of different shapes.

Synthesis of monodisperse iron-platinum (FePt) nanoparticles by reduction of platinum acetylacetonate and decomposition of iron pentacarbonyl in the presence of oleic acid and oleyl amine stabilizers is reported. The FePt particle composition is readily controlled, and the size is tunable from 3- to 10-nanometer diameter with a standard deviation of less than 5%. These nanoparticles self-assemble into three-dimensional superlattices. Thermal annealing converts the internal particle structure from a chemically disordered face-centered cubic phase to the chemically ordered face-centered tetragonal phase and transforms the nanoparticle superlattices into ferromagnetic nanocrystal assemblies. These assemblies are chemically and mechanically robust and can support high-density magnetization reversal transitions.

/pdf/monodisperse-fept-nanoparticles-and-ferromagnetic-fept-12j5xql32h.pdf

Monodisperse FePt Nanoparticles and Ferromagnetic FePt Nanocrystal Superlattices

Nanocrystals are fundamental to modern science and technology. Mastery over the shape of a nanocrystal enables control of its properties and enhancement of its usefulness for a given application. Our aim is to present a comprehensive review of current research activities that center on the shape-controlled synthesis of metal nanocrystals. We begin with a brief introduction to nucleation and growth within the context of metal nanocrystal synthesis, followed by a discussion of the possible shapes that a metal nanocrystal might take under different conditions. We then focus on a variety of experimental parameters that have been explored to manipulate the nucleation and growth of metal nanocrystals in solution-phase syntheses in an effort to generate specific shapes. We then elaborate on these approaches by selecting examples in which there is already reasonable understanding for the observed shape control or at least the protocols have proven to be reproducible and controllable. Finally, we highlight a number of applications that have been enabled and/or enhanced by the shape-controlled synthesis of metal nanocrystals. We conclude this article with personal perspectives on the directions toward which future research in this field might take.

Shape‐Controlled Synthesis of Metal Nanocrystals: Simple Chemistry Meets Complex Physics?

▪ Abstract Solution phase syntheses and size-selective separation methods to prepare semiconductor and metal nanocrystals, tunable in size from ∼1 to 20 nm and monodisperse to ≤5%, are presented. Preparation of monodisperse samples enables systematic characterization of the structural, electronic, and optical properties of materials as they evolve from molecular to bulk in the nanometer size range. Sample uniformity makes it possible to manipulate nanocrystals into close-packed, glassy, and ordered nanocrystal assemblies (superlattices, colloidal crystals, supercrystals). Rigorous structural characterization is critical to understanding the electronic and optical properties of both nanocrystals and their assemblies. At inter-particle separations 5–100 A, dipole-dipole interactions lead to energy transfer between neighboring nanocrystals, and electronic tunneling between proximal nanocrystals gives rise to dark and photoconductivity. At separations <5 A, exchange interactions cause otherwise insulating ass...

Synthesis and Characterization of Monodisperse Nanocrystals and Close-Packed Nanocrystal Assemblies

Nanocrystals (NCs) discussed in this Review are tiny crystals of metals, semiconductors, and magnetic material consisting of hundreds to a few thousand atoms each. Their size ranges from 2-3 to about 20 nm. What is special about this size regime that placed NCs among the hottest research topics of the last decades? The quantum mechanical coupling * To whom correspondence should be addressed. E-mail: dvtalapin@uchicago.edu. † The University of Chicago. ‡ Argonne National Lab. Chem. Rev. 2010, 110, 389–458 389

/pdf/prospects-of-colloidal-nanocrystals-for-electronic-and-3dxpyhl3r7.pdf

Prospects of Colloidal Nanocrystals for Electronic and Optoelectronic Applications

High temperature, solution phase reduction of cobalt chloride in the presence of stabilizing agents was employed to produce magnetic colloids (ferrofluids) of cobalt nanocrystals. We systematically synthesized and isolated nearly monodisperse nanocrystal samples ranging in size from 2 to 11 nm while maintaining better than a 7% std. dev. in diameter. As synthesized cobalt particles are each a single crystal with a complex cubic structure related to the beta phase of elemental manganese (e-Co). Annealing the nanocrystals at 300 °C converts them quantitatively to the more common hexagonal-close-packed crystal form. Deposition of these uniform cobalt particles on solid substrates by evaporation of the carrier solvent results in the spontaneous assembly of two-dimensional and three-dimensional magnetic superlattices (colloidal crystals). A combination of x-ray powder diffraction, transmission electron microscopy, and superconducting quantum interference device magnetometry were used to characterize both the d...

C. B. Murray

Papers

Synthesis of monodisperse cobalt nanocrystals and their assembly into magnetic superlattices (invited)