Harisankar Sreenivasan

Bio: Harisankar Sreenivasan is an academic researcher from University of Oulu. The author has contributed to research in topics: Tailings & Solubility. The author has an hindex of 10, co-authored 19 publications receiving 274 citations.

Immobilization of sulfates and heavy metals in gold mine tailings by sodium silicate and hydrated lime

Abstract: Gold mining produces hazardous tailings wastes with elevated sulfur content and high levels of heavy metals including oxyanion elements such as V and As. This research investigated activation of these tailings with calcium hydroxide and sodium hydroxide/sodium silicate as a way to stabilize the material and limit leaching of harmful components. The effects of thermal treatment on the reactivity of the tailings and the use of different activating solutions on the physical properties, microstructure and leaching of harmful components are reported. The effect of adding ground granulated blast furnace slag to the tailings is also assessed. The use of 5 wt % Ca(OH)2 activating solution produces optimum performance increasing the immobilization efficiency of sulfates, arsenic and the other harmful elements. Heat-treating mine tailings at 900 °C slightly improves the reactivity but did not improved the immobilization efficiency. Microstructural analysis by TEM and XRD confirmed that stabilization is based on calcium sulfate and/or ettringite formation during alkali-activation. All materials achieved reasonable compressive strength after 28 days of curing and the potential for using alkali activation as a method to treat tailings from mining is discussed.

Ag- or Cu-modified geopolymer filters for water treatment manufactured by 3D printing, direct foaming, or granulation.

Abstract: In this work, we compared the main characteristics of highly porous geopolymer components for water treatment applications manufactured by 3D printing, direct foaming, or granulation. Furthermore, different approaches to impregnate the materials with Ag or Cu were evaluated to obtain filters with disinfecting or catalytic properties. The results revealed that all of the investigated manufacturing methods enabled the fabrication of components that possessed mesoporosity, suitable mechanical strength, and water permeability, even though their morphologies were completely different. Total porosity and compressive strength values were 28 vol% and 16 MPa for 3D-printed, 70-79 vol% and 1 MPa for direct-foamed, and 27 vol% and 10 MPa for granule samples. Both the filter preparation and the metal impregnation method affected the amount, oxidation state, and stability of Ag and Cu in the filters. However, it was possible to prepare filters with low metal leaching between a pH of 3-7, so that the released Ag and Cu concentrations were within drinking water standards.

Understanding the Mechanisms of Lead, Copper, and Zinc Retention by Phosphate Rock

Abstract: The solid-liquid interface reaction between phosphate rock (PR) and metals (Pb, Cu, and Zn) was studied. Phosphate rock has the highest affinity for Pb, followed by Cu and Zn, with sorption capacities of 138, 114, and 83.2 mmol/kg PR, respectively. In the Pb-Cu-Zn ternary system, competitive metal sorption occurred with sorption capacity reduction of 15.2%, 48.3%, and 75.6% for Pb, Cu, and Zn, respectively compared to the mono-metal systems. A fractional factorial design showed the interfering effect in the order of Pb>Cu>Zn. Desorption of Cu and Zn was sensitive to pH change, increasing with pH decline, whereas Pb desorption was decreased with a strongly acidic TCLP extracting solution (pH = 2.93). The greatest stability of Pb retention by PR can be attributed to the formation of insoluble fluoropyromorphite [Pb(10)(PO(4))(6)F(2)], which was primarily responsible for Pb immobilization (up to 78.3%), with less contribution from the surface adsorption or complexation (21.7%), compared to 74.5% for Cu and 95.7% for Zn. Solution pH reduction during metal retention and flow calorimetry analysis both supported the hypothesis of retention of Pb, Cu, and Zn by surface adsorption or complexation. Flow calorimetry indicated that Pb and Cu adsorption onto PR was exothermic, while Zn sorption was endothermic. Our research demonstrated that PR can effectively remove Pb from solutions, even in the presence of other heavy metals (e.g. Cu, Zn).