Michael D. Weir

Bio: Michael D. Weir is an academic researcher from National Institute of Standards and Technology. The author has contributed to research in topics: Controlled release & Lower critical solution temperature. The author has an hindex of 9, co-authored 13 publications receiving 830 citations. Previous affiliations of Michael D. Weir include American Dental Association.

Strong Nanocomposites with Ca, PO4, and F Release for Caries Inhibition

Abstract: This article reviews recent studies on: (1) the synthesis of novel calcium phosphate and calcium fluoride nanoparticles and their incorporation into dental resins to develop nanocomposites; (2) the effects of key microstructural parameters on Ca, PO(4), and F ion release from nanocomposites, including the effects of nanofiller volume fraction, particle size, and silanization; and (3) mechanical properties of nanocomposites, including water-aging effects, flexural strength, fracture toughness, and three-body wear. This article demonstrates that a major advantage of using the new nanoparticles is that high levels of Ca, PO(4), and F release can be achieved at low filler levels in the resin, because of the high surface areas of the nanoparticles. This leaves room in the resin for substantial reinforcement fillers. The combination of releasing nanofillers with stable and strong reinforcing fillers is promising to yield a nanocomposite with both stress-bearing and caries-inhibiting capabilities, a combination not yet available in current materials.

Injectable and rapid-setting calcium phosphate bone cement with dicalcium phosphate dihydrate

Abstract: Calcium phosphate cement (CPC) sets in situ with intimate adaptation to the contours of defect surfaces, and forms an implant having a structure and composition similar to hydroxyapatite, the putative mineral in teeth and bones. The objective of the present study was to develop an injectable CPC using dicalcium phosphate dihydrate (DCPD) with a high solubility for rapid setting. Two agents were incorporated to impart injectability and fast-hardening to the cement: a hardening accelerator (sodium phosphate) and a gelling agent (hydroxypropyl methylcellulose, HPMC). The cement with DCPD was designated as CPC(D), and the conventional cement was referred to as CPC(A). Using water without sodium phosphate, CPC(A) had a setting time of 82 +/- 6 min. In contrast, CPC(D) exhibited rapid setting with a time of 17 +/- 1 min. At 0.2 mol/L sodium phosphate, setting time for CPC(D) was 15 +/- 1 min, significantly faster than 40 +/- 2 min for CPC(A) (Tukey's at 0.95). Sodium phosphate decreased the paste injectability (measured as the paste mass extruded from the syringe divided by the original paste mass inside the syringe). However, the addition of HPMC dramatically increased the paste injectability. For CPC(D), the injectability was increased from 65% +/- 12% without HPMC to 98% +/- 1% with 1% HPMC. Injectability of CPC(A) was also doubled to 99% +/- 1%. The injectable and rapid-setting CPC(D) possessed flexural strength and elastic modulus values overlapping the reported values for sintered porous hydroxyapatite implants and cancellous bone. In summary, the rapid setting and relatively high strength and elastic modulus of CPC(D) should help the graft to quickly attain strength and geometrical integrity within a short period of time postoperatively. Furthermore, the injectability of CPC(D) may have potential for procedures involving defects with limited accessibility or narrow cavities, when there is a need for precise placement of the paste, and when using minimally invasive surgical techniques.

Effects of Calcium Phosphate Nanoparticles on Ca-PO4 Composite

Abstract: Nano-particles of dicalcium phosphate anhydrous (DCPA) were synthesized for the first time. The objectives of this study were to incorporate DCPA nano-particles into resin for Ca-PO(4) release to combat dental caries, and to investigate the filler level effects. Nano-DCPA and nano-silica-fused silicon nitride whiskers at a 1:1 ratio were used at filler mass fractions of 0-75%. The flexural strengths in MPa (mean +/- SD; n = 6) of DCPA-whisker composites ranged from (106 +/- 39) at 0% fillers to (114 +/- 23) at 75% fillers, similar to (112 +/- 22) of a non-releasing composite (TPH) (p > 0.1). The composite with 75% fillers in a NaCl solution (133 mmol/L, pH = 7.4, 37 degrees C) yielded a Ca concentration of (0.65 +/- 0.02) mmol/L and PO(4) of (2.29 +/- 0.07) mmol/L. Relationships were established between ion-release and DCPA volume fraction V(DCPA): Ca = 4.46 V(DCPA)(1.6,) and = 66.9 V(DCPA)(2.6). Nano-DCPA-whisker PO(4) composites had high strength and released high levels of Ca-PO(4) requisite for remineralization. These new nano-composites could provide the needed combination of stress-bearing and caries-inhibiting capabilities.