R.O. Ritchie

Bio: R.O. Ritchie is an academic researcher from University of California, Berkeley. The author has contributed to research in topics: Brittleness. The author has an hindex of 1, co-authored 1 publications receiving 218 citations.

High-cycle fatigue of single-crystal silicon thin films

Abstract: When subjected to alternating stresses, most materials degrade, e.g., suffer premature failure, due to a phenomenon known as fatigue. It is generally accepted that in brittle materials, such as ceramics, fatigue can only take place in toughened solids, i.e., premature fatigue failure would not be expected in materials such as single crystal silicon. The results of this study, however, appear to be at odds with the current understanding of brittle material fatigue. Twelve thin-film (/spl sim/20 /spl mu/m thick) single crystal silicon specimens were tested to failure in a controlled air environment (30/spl plusmn/0.1/spl deg/C, 50/spl plusmn/2% relative humidity). Damage accumulation and failure of the notched cantilever beams were monitored electrically during the "fatigue life" test. Specimen lives ranged from about 10 s to 48 days, or 1/spl times/106 to 1/spl times/1011 cycles before failure over stress amplitudes ranging from approximately 4 to 10 GPa. A variety of mechanisms are discussed in light of the fatigue life data and fracture surface evaluation.

Failure mechanisms of single-crystal silicon electrodes in lithium-ion batteries

Abstract: Long-term durability is a major obstacle limiting the widespread use of lithium-ion batteries in heavy-duty applications and others demanding extended lifetime. As one of the root causes of the degradation of battery performance, the electrode failure mechanisms are still unknown. In this paper, we reveal the fundamental fracture mechanisms of single-crystal silicon electrodes over extended lithiation/delithiation cycles, using electrochemical testing, microstructure characterization, fracture mechanics and finite element analysis. Anisotropic lithium invasion causes crack initiation perpendicular to the electrode surface, followed by growth through the electrode thickness. The low fracture energy of the lithiated/unlithiated silicon interface provides a weak microstructural path for crack deflection, accounting for the crack patterns and delamination observed after repeated cycling. On the basis of this physical understanding, we demonstrate how electrolyte additives can heal electrode cracks and provide strategies to enhance the fracture resistance in future lithium-ion batteries from surface chemical, electrochemical and material science perspectives.

A review of MEMS-based microscale and nanoscale tensile and bending testing

Abstract: Thin films at the micrometer and submicrometer scales exhibit mechanical properties that are different than those of bulk polycrystals. Industrial application of these materials requires accurate mechanical characterization. Also, a fundamental understanding of the deformation processes at smaller length scales is required to exploit the size and interface effects to develop new and technologically attractive materials. Specimen fabrication, small-scale force and displacement generation, and high resolution in the measurements are generic challenges in microscale and nanoscale mechanical testing. In this paper, we review small-scale materials testing techniques with special focus on the application of microelectromechanical systems (MEMS). Small size and high force and displacement resolution make MEMS suitable for small-scale mechanical testing. We discuss the development of tensile and bending testing techniques using MEMS, along with the experimental results on nanoscale aluminum specimens.

High-cycle fatigue and durability of polycrystalline silicon thin films in ambient air

Abstract: To evaluate the long-term durability properties of materials for microelectromechanical systems (MEMS), the stress-life ( S / N ) cyclic fatigue behavior of a 2-μm thick polycrystalline silicon film was evaluated in laboratory air using an electrostatically actuated notched cantilever beam resonator. A total of 28 specimens were tested for failure under high frequency (∼40 kHz) cyclic loads with lives ranging from about 10 s to 34 days (3×10 5 to 1.2×10 11 cycles) over fully reversed, sinusoidal stress amplitudes varying from ∼2.0 to 4.0 GPa. The thin-film polycrystalline silicon cantilever beams exhibited a time-delayed failure that was accompanied by a continuous increase in the compliance of the specimen. This apparent cyclic fatigue effect resulted in an endurance strength, at greater than 10 9 cycles, of ∼2 GPa, i.e. roughly one-half of the (single cycle) fracture strength. Based on experimental and numerical results, the fatigue process is attributed to a novel mechanism involving the environmentally-assisted cracking of the surface oxide film (termed reaction-layer fatigue). These results provide the most comprehensive, high-cycle, endurance data for designers of polysilicon micromechanical components available to date.

Fatigue failure in polysilicon not due to simple stress corrosion cracking.

Abstract: In the absence of a corrosive environment, brittle materials such as silicon should be immune to cyclic fatigue However, fatigue effects are well known in micrometer-sized polycrystalline silicon (polysilicon) samples tested in air To investigate the origins of this phenomenon in polysilicon, we developed a fixed-grip fracture mechanics microspecimen but could find no evidence of static stress corrosion cracking The environmental sensitivity of the fatigue resistance was also investigated under cyclic loading For low-cycle fatigue, the behavior is independent of the ambient conditions, whether air or vacuum, but is strongly influenced by the ratio of compressive to tensile stresses experienced during each cycle The fatigue damage most likely originates from contact stresses at processing-related surface asperities; subcritical crack growth then ensues during further cyclic loading The lower far-field stresses involved in high-cycle fatigue induce reduced levels of fatigue damage Under these conditions, a corrosive ambient such as laboratory air exacerbates the fatigue process Without cyclic loading, polysilicon does not undergo stress corrosion cracking