Use of amphiphilic triblock copolymers to direct the organization of polymerizing silica species has resulted in the preparation of well-ordered hexagonal mesoporous silica structures (SBA-15) with uniform pore sizes up to approximately 300 angstroms. The SBA-15 materials are synthesized in acidic media to produce highly ordered, two-dimensional hexagonal (space group p6mm) silica-block copolymer mesophases. Calcination at 500°C gives porous structures with unusually large interlattice d spacings of 74.5 to 320 angstroms between the (100) planes, pore sizes from 46 to 300 angstroms, pore volume fractions up to 0.85, and silica wall thicknesses of 31 to 64 angstroms. SBA-15 can be readily prepared over a wide range of uniform pore sizes and pore wall thicknesses at low temperature (35° to 80°C), using a variety of poly(alkylene oxide) triblock copolymers and by the addition of cosolvent organic molecules. The block copolymer species can be recovered for reuse by solvent extraction with ethanol or removed by heating at 140°C for 3 hours, in both cases, yielding a product that is thermally stable in boiling water.

Triblock copolymer syntheses of mesoporous silica with periodic 50 to 300 angstrom pores

A family of highly ordered mesoporous (20−300 A) silica structures have been synthesized by the use of commercially available nonionic alkyl poly(ethylene oxide) (PEO) oligomeric surfactants and poly(alkylene oxide) block copolymers in acid media. Periodic arrangements of mescoscopically ordered pores with cubic Im3m, cubic Pm3m (or others), 3-d hexagonal (P63/mmc), 2-d hexagonal (p6mm), and lamellar (Lα) symmetries have been prepared. Under acidic conditions at room temperature, the nonionic oligomeric surfactants frequently form cubic or 3-d hexagonal mesoporous silica structures, while the nonionic triblock copolymers tend to form hexagonal (p6mm) mesoporous silica structures. A cubic mesoporous silica structure (SBA-11) with Pm3m diffraction symmetry has been synthesized in the presence of C16H33(OCH2CH2)10OH (C16EO10) surfactant species, while a 3-d hexagonal (P63/mmc) mesoporous silica structure (SBA-12) results when C18EO10 is used. Surfactants with short EO segments tend to form lamellar mesost...

Nonionic Triblock and Star Diblock Copolymer and Oligomeric Surfactant Syntheses of Highly Ordered, Hydrothermally Stable, Mesoporous Silica Structures

It is possible to say that zeolites are the most widely used catalysts in industry They are crystalline microporous materials which have become extremely successful as catalysts for oil refining, petrochemistry, and organic synthesis in the production of fine and speciality chemicals, particularly when dealing with molecules having kinetic diameters below 10 A The reason for their success in catalysis is related to the following specific features of these materials:1 (1) They have very high surface area and adsorption capacity (2) The adsorption properties of the zeolites can be controlled, and they can be varied from hydrophobic to hydrophilic type materials (3) Active sites, such as acid sites for instance, can be generated in the framework and their strength and concentration can be tailored for a particular application (4) The sizes of their channels and cavities are in the range typical for many molecules of interest (5-12 A), and the strong electric fields2 existing in those micropores together with an electronic confinement of the guest molecules3 are responsible for a preactivation of the reactants (5) Their intricate channel structure allows the zeolites to present different types of shape selectivity, ie, product, reactant, and transition state, which can be used to direct a given catalytic reaction toward the desired product avoiding undesired side reactions (6) All of these properties of zeolites, which are of paramount importance in catalysis and make them attractive choices for the types of processes listed above, are ultimately dependent on the thermal and hydrothermal stability of these materials In the case of zeolites, they can be activated to produce very stable materials not just resistant to heat and steam but also to chemical attacks Avelino Corma Canos was born in Moncofar, Spain, in 1951 He studied chemistry at the Universidad de Valencia (1967−1973) and received his PhD at the Universidad Complutense de Madrid in 1976 He became director of the Instituto de Tecnologia Quimica (UPV-CSIC) at the Universidad Politecnica de Valencia in 1990 His current research field is zeolites as catalysts, covering aspects of synthesis, characterization and reactivity in acid−base and redox catalysis A Corma has written about 250 articles on these subjects in international journals, three books, and a number of reviews and book chapters He is a member of the Editorial Board of Zeolites, Catalysis Review Science and Engineering, Catalysis Letters, Applied Catalysis, Journal of Molecular Catalysis, Research Trends, CaTTech, and Journal of the Chemical Society, Chemical Communications A Corma is coauthor of 20 patents, five of them being for commercial applications He has been awarded with the Dupont Award on new materials (1995), and the Spanish National Award “Leonardo Torres Quevedo” on Technology Research (1996) 2373 Chem Rev 1997, 97, 2373−2419

From Microporous to Mesoporous Molecular-Sieve Materials and Their Use in Catalysis

The Li-S battery has been under intense scrutiny for over two decades, as it offers the possibility of high gravimetric capacities and theoretical energy densities ranging up to a factor of five beyond conventional Li-ion systems. Herein, we report the feasibility to approach such capacities by creating highly ordered interwoven composites. The conductive mesoporous carbon framework precisely constrains sulphur nanofiller growth within its channels and generates essential electrical contact to the insulating sulphur. The structure provides access to Li+ ingress/egress for reactivity with the sulphur, and we speculate that the kinetic inhibition to diffusion within the framework and the sorption properties of the carbon aid in trapping the polysulphides formed during redox. Polymer modification of the carbon surface further provides a chemical gradient that retards diffusion of these large anions out of the electrode, thus facilitating more complete reaction. Reversible capacities up to 1,320 mA h g(-1) are attained. The assembly process is simple and broadly applicable, conceptually providing new opportunities for materials scientists for tailored design that can be extended to many different electrode materials.

http://dns2.asia.edu.tw/~ysho/YSHO-English/1000%20WC/PDF/Nat%20Mat8,%20500.pdf

A highly ordered nanostructured carbon–sulphur cathode for lithium–sulphur batteries

"Space—the final frontier." This preamble to a well-known television series captures the challenge encountered not only in space travel adventures, but also in the field of porous materials, which aims to control the size, shape and uniformity of the porous space and the atoms and molecules that define it. The past decade has seen significant advances in the ability to fabricate new porous solids with ordered structures from a wide range of different materials. This has resulted in materials with unusual properties and broadened their application range beyond the traditional use as catalysts and adsorbents. In fact, porous materials now seem set to contribute to developments in areas ranging from microelectronics to medical diagnosis.

Ordered porous materials for emerging applications

R.R. is thankful for financial support by Korean Research Foundation (1998-010-180). M.J. and M.K. acknowledge donors of the Petroleum Research Fund administered by the American Chemical Society. O.T. and Z.L. thank CREST, JST for supports.

Synthesis of New, Nanoporous Carbon with Hexagonally Ordered Mesostructure

Ordered carbon molecular sieves exhibiting Bragg diffraction of X-ray lines have been synthesized for the first time, using mesoporous silica molecular sieves as the template. Sucrose was converted to carbon inside the mesopores of the silica molecular sieves through a mild carbonization process using a sulfuric acid catalyst. The carbon molecular sieves were obtained after the removal of the silica framework using an aqueous solution of sodium hydroxide. The X-ray diffraction, transmission electron microscopy, and pore size analysis showed that the structure of the carbon molecular sieves consisted of a three-dimensional regular array of uniform mesopores 3 nm in diameter. The structure was not simply a negative replica of the used silica template, but the synthesis mechanism involved the unique transformation into a new ordered array that was triggered by the removal of the silica frameworks. The highly ordered mesoporous texture suggested its scientific and technological importance as a new shape-selec...

Synthesis of highly ordered carbon molecular sieves via template-mediated structural transformation

Ion exchange and thermal stability of mcm-41

Low hydrothermal stability in hot water and aqueous solutions was a critical problem for many applications of the mesoporous molecular sieve MCM-41, compared with conventional zeolites such as Y and ZSM-5. The hydrothermal stability of MCM-41 has been found to improve remarkably by using various salts such as sodium chloride, potassium chloride, sodium acetate, and ethylenediaminetetraacetic acid tetrasodium salt during the hydrothermal crystallization process performed at 370 K. High-quality MCM-41 samples obtained by using the salt effect indicated negligible structural losses as judged by X-ray diffraction during heating for 12 h in boiling water.

Shinae Jun

Papers

Synthesis of New, Nanoporous Carbon with Hexagonally Ordered Mesostructure

Synthesis of highly ordered carbon molecular sieves via template-mediated structural transformation

Ion exchange and thermal stability of mcm-41

Improvement of Hydrothermal Stability of MCM-41 Using Salt Effects during the Crystallization Process

Synthesis of ordered mesoporous carbon molecular sieves CMK-1