Cochin University of Science and Technology

About: Cochin University of Science and Technology is a education organization based out in Kochi, Kerala, India. It is known for research contribution in the topics: Thin film & Natural rubber. The organization has 5382 authors who have published 7690 publications receiving 103827 citations. The organization is also known as: CUSAT & Cochin University.

Growth and characterization of tin oxide thin films and fabrication of transparent p-SnO/n-ZnO p–n hetero junction

Abstract: p-Type and n-type tin oxide thin films were deposited by rf-magnetron sputtering of metal tin target by varying the oxygen pressure. Chemical composition of SnO thin film according to the intensity of the XPS peak is about 48.85% and 51.15% for tin and oxygen respectively. Nearest neighbor distance of the atoms calculated from SAED patterns is 2.9 Aand 2.7 Afor SnO and SnO 2 respectively. The Raman scattering spectrum obtained from SnO thin films showed two peaks, one at 113 cm −1 and the other at 211 cm −1 . Band gap of as-deposited SnO x thin films vary from 1.6 eV to 3.2 eV on varying the oxygen partial pressure from 3% to 30% which indicates the oxidization of metallic phase Sn to SnO and SnO 2 . p-Type conductivity of SnO thin films and n-type conductivity of SnO 2 thin films were confirmed through Hall coefficient measurement. Transparent p–n hetero junction fabricated in the structure glass/ITO/n-ZnO/p-SnO shows rectification with forward to reverse current ratio as 12 at 4.5 V.

Optoelectronic properties and Seebeck coefficient in SnSe thin films

Abstract: SnSe thin films of thickness 180 nm have been deposited on glass substrates by reactive evaporation at an optimized substrate temperature of 523 ± 5 K and pressure of 10−5 mbar. The as-prepared SnSe thin films are characterized for their structural, optical and electrical properties by various experimental techniques. The p-type conductivity, near-optimum direct band gap, high absorption coefficient and good photosensitivity of the SnSe thin film indicate its suitability for photovoltaic applications. The optical constants, loss factor, quality factor and optical conductivity of the films are evaluated. The results of Hall and thermoelectric power measurements are correlated to determine the density of states, Fermi energy and effective mass of carriers and are obtained as 2.8 × 1017 cm−3, 0.03 eV and 0.05m 0 respectively. The high Seebeck coefficient ≈ 7863 μV/K, reasonably good power factor ≈ 7.2 × 10−4 W/(mK2) and thermoelectric figure of merit ≈ 1.2 observed at 42 K suggests that, on further work, the prepared SnSe thin films can also be considered as a possible candidate for cryogenic thermoelectric applications.

Design and fabrication of an E-shaped wearable textile antenna on PVB-coated hydrophobic polyester fabric

Abstract: In this paper, we investigated the simulation and fabrication of an E-shaped microstrip patch antenna realized on multilayered polyester fabric suitable for WiMAX (Worldwide Interoperability for Microwave Access) applications. The main challenges while designing a textile antenna were to provide adequate thickness, surface uniformity and water wettability to the textile substrate. Here, three layers of polyester fabric were stacked together in order to obtain sufficient thickness, and were subsequently dip coated with polyvinyl butyral (PVB) solution. The PVB-coated polyester fabric showed a hydrophobic nature with a contact angle of 91°. The RMS roughness of the uncoated and PVB-coated polyester fabric was about 341 nm and 15 nm respectively. The promising properties, such as their flexibility, light weight and cost effectiveness, enable effortless integration of the proposed antenna into clothes like polyester jackets. Simulated and measured results in terms of return loss as well as gain were showcased to confirm the usefulness of the fabricated prototype. The fabricated antenna successfully operates at 3.37 GHz with a return loss of 21 dB and a maximum measured gain of 3.6 dB.