Open AccessJournal Article
Effect of Resin Impregnation Rate on Physical and Mechanical Properties of Laminated Bamboo Fibrillated-Veneer Lumber
Reads0
Chats0
TLDR
In this article, the effect of resin impregnation rate on mechanical performance and water resistance was discussed, and it was shown that increasing specimen resin content from 7% to 13% had a negative impact on the average modulus of rupture (MOR) and tensile strength, and a positive influence on the shear strength and water resistant.Abstract:
The authors developed a new technology for making laminated fibrillated-veneer lumber.They designed an experiment using bamboo(Bambusa distegia) to optimize the processing parameters.The effect of resin impregnation rate on mechanical performance and water resistance was discussed.The results showed that increasing specimen resin content from 7% to 13%,had a negative impact on the average modulus of rupture(MOR) and tensile strength,and a positive influence on the shear strength and water resistance.However,the increase in resin content didn't affect the modulus of elasticity(MOE) or compression strength.The authors suggested that the panel's mechanical performance and water resistance could be predicted by controlling the resin impregnation level to meet different application demands.read more
Citations
More filters
Journal ArticleDOI
Fabrication, material properties, and application of bamboo scrimber
TL;DR: In this article, the water absorption, dimensional stability, and mechanical properties of the bamboo scrimbers were determined, and a bamboo scrimber made from bamboo bundles processed at 180°C hot dry air treatment combined with 18% PF resin loading showed good technological properties.
Journal ArticleDOI
Evaluation of the Uniformity of Density and Mechanical Properties of Bamboo-Bundle Laminated Veneer Lumber (BLVL)
Fuming Chen,Zehui Jiang,Jianchao Deng,Ge Wang,Dan Zhang,Qingchao Zhao,Liping Cai,Sheldon Q. Shi +7 more
TL;DR: In this article, the authors evaluated the uniformity of density distribution for Bamboo-bundle Laminated Veneer Lumber (BLVL) and its relationship to the stability of mechanical performance.
Journal ArticleDOI
Progress of Bamboo Recombination Technology in China
TL;DR: Wang et al. as mentioned in this paper reviewed the research process and progress of bamboo recombination technology, the existing technical problems and prospects, in order to provide references for future research on biomolecular recombination theory and production practice.
Journal ArticleDOI
Effect of Steam Heating on the Color and Chemical Properties of Neosinocalamus Affinis Bamboo
Yamei Zhang,Wenji Yu,Yahui Zhang +2 more
TL;DR: In this paper, steam treatment of the fibrous veneers was performed inside an autoclave at 0.35 MPa to 0.45 MPa (147°C to 155°C) for 110min to 170min.
Journal ArticleDOI
Impact properties of bamboo bundle laminated veneer lumber by preprocessing densification technology
Fuming Chen,Jianchao Deng,Haitao Cheng,Haidong Li,Zehui Jiang,Ge Wang,Qingchao Zhao,Sheldon Q. Shi +7 more
TL;DR: In this paper, the deformation behavior of laminated veneer lumber (BLVL) was investigated under low velocity impact loading, and the influence of different preprocessing temperatures, times, and stacking sequences was studied with respect to impact loading.
Related Papers (5)
Effects of resin impregnation and process parameters on some properties of poplar LVL
Experimental Design on Laminated Veneer Lumber Fiber Reinforced Composite: Processing Parameters and Its Durability
Utai Meekum,Yumatorn Mingmongkol +1 more