TL;DR: The fabrication of transparent field-effect transistors using a single-crystalline thin-film transparent oxide semiconductor, InGaO3(ZnO)5, as an electron channel and amorphous hafnium oxide as a gate insulator provides a step toward the realization of transparent electronics for next-generation optoelectronics.
Abstract: We report the fabrication of transparent field-effect transistors using a single-crystalline thin-film transparent oxide semiconductor, InGaO 3 (ZnO) 5 , as an electron channel and amorphous hafnium oxide as a gate insulator. The device exhibits an on-to-off current ratio of ∼10 6 and a field-effect mobility of ∼80 square centimeters per volt per second at room temperature, with operation insensitive to visible light irradiation. The result provides a step toward the realization of transparent electronics for next-generation optoelectronics.
2,724 citations
TL;DR: In this article, the authors showed that nanometre-sized ceramic powders can be used as solid plasticizers for polyethylene oxide (PEO) electrolytes to prevent crystallization on annealing from amorphous state above 60°C.
Abstract: Ionically conducting polymer membranes (polymer electrolytes) might enhance lithium-battery technology by replacing the liquid electrolyte currently in use and thereby enabling the fabrication of flexible, compact, laminated solid-state structures free from leaks and available in varied geometries1. Polymer electrolytes explored for these purposes are commonly complexes of a lithium salt (LiX) with a high-molecular-weight polymer such as polyethylene oxide (PEO). But PEO tends to crystallize below 60 °C, whereas fast ion transport is a characteristic of the amorphous phase. So the conductivity of PEO–LiX electrolytes reaches practically useful values (of about 10−4 S cm−1) only at temperatures of 60–80 °C. The most common approach for lowering the operational temperature has been to add liquid plasticizers, but this promotes deterioration of the electrolyte's mechanical properties and increases its reactivity towards the lithium metal anode. Here we show that nanometre-sized ceramic powders can perform as solid plasticizers for PEO, kinetically inhibiting crystallization on annealing from the amorphous state above 60 °C. We demonstrate conductivities of around 10−4 S cm−1 at 50 °C and 10−5 S cm−1 at 30 °C in a PEO–LiClO4 mixture containing powders of TiO2 and Al2O3 with particle sizes of 5.8–13 nm. Further optimization might lead to practical solid-state polymer electrolytes for lithium batteries.
2,695 citations
TL;DR: In this paper, a new reversible photoelectronic effect was reported for amorphous Si produced by glow discharge of SiH4, where long exposure to light decreases both the photoconductivity and the dark conductivity.
Abstract: A new reversible photoelectronic effect is reported for amorphous Si produced by glow discharge of SiH4. Long exposure to light decreases both the photoconductivity and the dark conductivity, the latter by nearly four orders of magnitude. Annealing above 150 °C reverses the process. A model involving optically induced changes in gap states is proposed. The results have strong implications for both the physical nature of the material and for its applications in thin‐film solar cells, as well as the reproducibility of measurements on discharge‐produced Si.
2,673 citations
TL;DR: A tin-based amorphous composite oxide (TCO) was synthesized in this paper to replace the carbon-based lithium intercalation materials currently in extensive use as the negative electrode (anode) of lithium-ion rechargeable batteries.
Abstract: A high-capacity lithium-storage material in metal-oxide form has been synthesized that can replace the carbon-based lithium intercalation materials currently in extensive use as the negative electrode (anode) of lithium-ion rechargeable batteries. This tin-based amorphous composite oxide (TCO) contains Sn(II)-O as the active center for lithium insertion and other glass-forming elements, which make up an oxide network. The TCO anode yields a specific capacity for reversible lithium adsorption more than 50 percent higher than those of the carbon families that persists after charge-discharge cycling when coupled with a lithium cobalt oxide cathode. Lithium-7 nuclear magnetic resonance measurements evidenced the high ionic state of lithium retained in the charged state, in which TCO accepted 8 moles of lithium ions per unit mole.
2,470 citations
TL;DR: In this article, the analysis of the infrared absorption bands in amorphous Ge which correspond to transitions between the three branches of the valence band has shown that the wave functions are delocalized over distances of the order 102A.
2,470 citations