TL;DR: In this paper, the hardness and elastic modulus of aluminum films with thicknesses of 240, 650, and 1700 nm sputter-deposited on glass were systematically characterized as a function of indenter penetration depth using standard nanoindentation methods.
Abstract: Substrate effects on the measurement of thin film mechanical properties by nanoindentation methods have been studied experimentally using a model soft film on hard substrate system: aluminum on glass. The hardness and elastic modulus of aluminum films with thicknesses of 240, 650, and 1700 nm sputter-deposited on glass were systematically characterized as a function of indenter penetration depth using standard nanoindentation methods. Scanning electron and atomic force microscopy of the hardness impressions revealed that indentation pileup in the aluminum is significantly enhanced by the substrate. The substrate also affects the form of the unloading curve in a manner that has important implications for nanoindentation data analysis procedures. Because of these effects, nanoindentation measurement techniques overestimate the film hardness and elastic modulus by as much as 100% and 50%, respectively, depending on the indentation depth. The largest errors occur at depths approximately equal to the film thickness.
342 citations
••
TL;DR: In this paper, the hardness and elastic modulus were measured using nanoindentation methods, and ultra-low load scratch tests were used to assess the scratch resistance of the films and measure friction coefficients.
Abstract: Nanoindentation and nanoscratching experiments have been performed to assess the mechanical properties of several carbon thin films with potential application as wear resistant coatings for magnetic disks. These include three hydrogenated-carbon films prepared by sputter deposition in a H{sub 2}/Ar gas mixture (hydrogen contents of 20, 34, and 40 atomic %) and a pure carbon film prepared by cathodic-arc plasma techniques. Each film was deposited on a silicon substrate to thickness of about 300 run. The hardness and elastic modulus were measured using nanoindentation methods, and ultra-low load scratch tests were used to assess the scratch resistance of the films and measure friction coefficients. Results show that the hardness, elastic modulus, and scratch resistance of the 20 and 34% hydrogenated films are significantly greater than the 40% film, thereby showing that there is a limit to the amount of hydrogen producing beneficial effects. The cathodic-arc film, with a hardness of greater than 59 GPa, is considerably harder than any of the hydrogenated films and has a superior scratch resistance.
342 citations
••
TL;DR: This paper presents ElaStic, a tool that is able to calculate the full second-order elastic stiffness tensor for any crystal structure from total-energy and/or stress calculations, and proposes a new approach to obtain the most reliable results.
341 citations
••
TL;DR: In this article, the hardness and elastic modulus of a silver nanowire was measured using a nanoindenter, and it was found that the nanoindentable wire has comparable hardness to bulk silver.
Abstract: The hardness and elastic modulus of a silver nanowire was measured using a nanoindenter. It was found that the silver nanowire has comparable hardness and elastic modulus to bulk silver. An array of nanoscale indents was successfully made on the wire by directly indenting the wire. The shape and size of the indents are controllable. The nanoindentation approach permits the direct machining of nanowires without the complications of conventional lithography.
341 citations
••
TL;DR: In this paper, an experimental study was conducted to investigate anisotropy effects on tensile properties of two short glass fiber reinforced thermoplastics, and mechanisms of failure were identified based on fracture surface microscopic analysis and crack propagation paths.
Abstract: An experimental study was conducted to investigate anisotropy effects on tensile properties of two short glass fiber reinforced thermoplastics. Tensile tests were performed in various mold flow directions and with two thicknesses. A shell–core morphology resulting from orientation distribution of fibers influenced the degree of anisotropy. Tensile strength and elastic modulus nonlinearly decreased with specimen angle and Tsai–Hill criterion was found to correlate variation of these properties with the fiber orientation. Variation of tensile toughness with fiber orientation and strain rate was evaluated and mechanisms of failure were identified based on fracture surface microscopic analysis and crack propagation paths. Fiber length, diameter, and orientation distribution mathematical models were also used along with analytical approaches to predict tensile strength and elastic modulus form tensile properties of constituent materials. Laminate analogy and modified Tsai–Hill criteria provided satisfactory predictions of elastic modulus and tensile strength, respectively.
340 citations