Fractography

About: Fractography is a research topic. Over the lifetime, 5043 publications have been published within this topic receiving 86068 citations.

Fracture and failure behavior of fabric-reinforced all-poly(propylene) composite (Curv®)

Abstract: The in-plane static fracture of a fabric reinforced all-poly(propylene) (all-PP, Curv®) composite was studied at ambient temperature using the concept of the linear elastic fracture mechanics. The apparent fracture toughness was determined on single-edge notched tensile specimens (SEN-T) considering the maximum load. The related values did not differ much from those determined by the resistance curve (KR) method. The crack growth, requested to construct the KR curves, was traced by the movement in the center of gravity of the cumulative amplitude of the located acoustic emission (AE) events. The quality of consolidation of the all-PP composite was reflected by the force-displacement curve (appearance of pop-in), course of the cumulative AE events during loading, extension and change of the estimated damage zone during fracture. The failure behavior was studied also by fractography and is discussed. Copyright © 2006 John Wiley & Sons, Ltd.

The Blast Behavior of Fiber Reinforced Thermoplastic Laminates

Abstract: This article presents the results of a series of blast tests on a carbon fiber-reinforced poly-ether-imide (PEI) and a glass fiber-reinforced PEI composite. Initially, the fracture properties of the two composite systems were characterized through a series of flexural and interlaminar fracture tests. Blast testing was then undertaken on a ballistic pendulum facility, capable of measuring the impulse imparted by the plastic explosive. Delamination, localized fiber buckling, fiber fracture, and shear failure at the boundary of the clamped plates were identified as the primary failure mechanisms in the laminates, with their severity depending on the panel thickness and the applied impulse. Delamination was very localized along the center plane of the laminate, a reflection of the very high interlaminar fracture toughness of these composites. The critical impulse for rear surface fiber fracture has been found to increase rapidly with laminate thickness for the range of panels considered here. The impulses associated with the onset of rear-surface fiber fracture and complete failure of the target were similar, suggesting that rear surface fiber fracture is a pre-cursor to complete failure in these laminates. Limited tests on the glass fiber-reinforced PEI system showed that it offers a superior blast resistance to its carbon fiber counterpart.