Friction stir processing

Abstract: Friction stir welding (FSW) is a relatively new solid-state joining process. This joining technique is energy efficient, environment friendly, and versatile. In particular, it can be used to join high-strength aerospace aluminum alloys and other metallic alloys that are hard to weld by conventional fusion welding. FSW is considered to be the most significant development in metal joining in a decade. Recently, friction stir processing (FSP) was developed for microstructural modification of metallic materials. In this review article, the current state of understanding and development of the FSW and FSP are addressed. Particular emphasis has been given to: (a) mechanisms responsible for the formation of welds and microstructural refinement, and (b) effects of FSW/FSP parameters on resultant microstructure and final mechanical properties. While the bulk of the information is related to aluminum alloys, important results are now available for other metals and alloys. At this stage, the technology diffusion has significantly outpaced the fundamental understanding of microstructural evolution and microstructure–property relationships.

Abstract: Friction stir processing (FSP), developed based on the basic principles of friction stir welding (FSW), a solid-state joining process originally developed for aluminum alloys, is an emerging metalworking technique that can provide localized modification and control of microstructures in near-surface layers of processed metallic components. The FSP causes intense plastic deformation, material mixing, and thermal exposure, resulting in significant microstructural refinement, densification, and homogeneity of the processed zone. The FSP technique has been successfully used for producing the fine-grained structure and surface composite, modifying the microstructure of materials, and synthesizing the composite and intermetallic compound in situ. In this review article, the current state of the understanding and development of FSP is addressed.

Abstract: A novel surface modifying technique, friction stir processing (FSP), has been developed for fabrication of surface composite. Al–SiC surface composites with different volume fractions of particles were successfully fabricated. The thickness of the surface composite layer ranged from 50 to 200 μm. The SiC particles were uniformly distributed in the aluminum matrix. The surface composites have excellent bonding with the aluminum alloy substrate. The microhardness of the surface composite reinforced with 27vol.%SiC of 0.7 μm average particle size was ∼173 HV, almost double of the 5083Al alloy substrate (85 HV). The solid-state processing and very fine microstructure that results are also desirable for high performance surface composites.

Abstract: In this paper, the authors report the first results using friction stir processing (FSP). In the last ten years, a new technique of Friction Stir Welding (FSW) has emerged as an exciting solid state joining technique for aluminum alloys. This technique, developed by The Welding Institute (TWI), involves traversing a rotating tool that produces intense plastic deformation through a stirring action. The localized heating is produced by friction between the tool shoulder and the sheet top surface, as well as plastic deformation of the material in contact with the tool. This results in a stirred zone with a very fine grain size in a single pass. Mahoney et al. observed a grain size of 3 {micro}m in a 7075 Al alloy. This process can be easily adopted as a processing technique to obtain fine grain size. FSP of a commercial 7075 Al alloy resulted in significant enhancement of superplastic properties. The optimum superplastic strain rate was 10{sup {minus}2}s{sup {minus}1} at 490 C in the FSP 7075 Al alloy, an improvement of more than an order of magnitude in strain rate. The present results suggest an exciting possibility to use a simple FSP technique to enhance grain size dependent properties.

Abstract: The relationship between the resulting grain size and the applied working strain rate and temperature for the friction stir processing in AZ31 Mg is systemically examined. The Zener–Holloman parameter is utilized in rationalizing the relationship. The grain orientation distribution is also studied using the X-ray diffraction.