Light-emitting diode

Abstract: A novel electroluminescent device is constructed using organic materials as the emitting elements. The diode has a double‐layer structure of organic thin films, prepared by vapor deposition. Efficient injection of holes and electrons is provided from an indium‐tin‐oxide anode and an alloyed Mg:Ag cathode. Electron‐hole recombination and green electroluminescent emission are confined near the organic interface region. High external quantum efficiency (1% photon/electron), luminous efficiency (1.5 lm/W), and brightness (>1000 cd/m2) are achievable at a driving voltage below 10 V.

Abstract: Physics of gallium nitrides and related compounds GaN growth p-Type GaN obtained by electron beam irradiation n-Type GaN p-Type GaN InGaN Zn and Si co-doped InGaN/AlGaN double-heterostructure blue and blue-green LEDs inGaN single-quantum-well structure LEDs room-temperature pulsed operation of laser diodes emission mechanisms of LEDs and LDs room temperature CW operation of InGaN MQW LDs latest results - lasers with self-organized InGaN quantum dots

Abstract: ELECTROLUMINESCENT devices have been developed recently that are based on new materials such as porous silicon1 and semiconducting polymers2,3. By taking advantage of developments in the preparation and characterization of direct-gap semiconductor nanocrystals4–6, and of electroluminescent polymers7, we have now constructed a hybrid organic/inorganic electroluminescent device. Light emission arises from the recombination of holes injected into a layer of semiconducting p-paraphenylene vinylene (PPV)8–10 with electrons injected into a multilayer film of cadmium selenide nanocrystals. Close matching of the emitting layer of nanocrystals with the work function of the metal contact leads to an operating voltage11 of only 4V. At low voltages emission from the CdSe layer occurs. Because of the quantum size effect19–24 the colour of this emission can be varied from red to yellow by changing the nanocrystal size. At higher voltages green emission from the polymer layer predominates. Thus this device has a degree of voltage tunability of colour.

Abstract: Candela‐class high‐brightness InGaN/AlGaN double‐heterostructure (DH) blue‐light‐emitting diodes(LEDs) with the luminous intensity over 1 cd were fabricated As an active layer, a Zn‐doped InGaN layer was used for the DH LEDs The typical output power was 1500 μW and the external quantum efficiency was as high as 27% at a forward current of 20 mA at room temperature The peak wavelength and the full width at half‐maximum of the electroluminescence were 450 and 70 nm, respectively This value of luminous intensity was the highest ever reported for blue LEDs

Abstract: ELECTROLUMINESCENT devices have been developed recently that are based on new materials such as porous silicon' and semiconducting polymers 2,3 . By taking advantage of developments in the preparation and characterization of direct-gap semiconductor nanocrystals 4-6 , and of electroluminescent polymers7, we have now constructed a hybrid organic/inorganic electroluminescent device. Light emission arises from the recombination of holes injected into a layer of semiconducting p-paraphenylene vinylene (PPV) 2-10 with electrons injected into a multilayer film of cadmium selenide nanocrystals. Close matching of the emitting layer of nanocrystals with the work function of the metal contact leads to an operating voltage" of only 4 V. At low voltages emission from the CdSe layer occurs. Because of the quantum size effect 19-24 the colour of this emission can be varied from red to yellow by changing the nanocrystal size. At higher voltages green emission from the polymer layer predominates. Thus this device has a degree of voltage tunability of colour.