TIG welding with single-component fluxes

Increasing the oxygen or the carbon dioxide concentration in the argon-based shielding gas leads to an increase in the weld metal oxygen content when the oxygen or carbon dioxide concentration is to be lower than 0.6 vol.% in the shielding gas. However, when the O2 or CO2 concentration is higher than 0.6 vol.% in the Ar-based shielding gas, the weld metal oxygen is maintained around 200 ppm–250 ppm. An inward Marangoni convection mode in the weld pool occurs when the weld metal oxygen content is more than 100 ppm. When it is lower than 100 ppm, the Marangoni convection would change to the outward direction and the weld shape varies from a deep narrow to a shallow wide shape. The effective ranges of O2 and CO2 concentrations for deep penetration are same. A heavy layer of oxides is formed when the O2 or CO2 concentration in the shielding gas is more than 0.6 vol.%. Based on the thermodynamic calculation of the equilibrium reactions of Fe, Si, Cr and Mn with oxygen in liquid iron for the oxide products, FeO, SiO2 ,C r 2O3 and MnO and the experimental oxygen content in the weld metal, Cr2O3 and SiO2 oxides are possibly formed at the periphery area of the liquid pool surface under the arc column during the welding process. One model is proposed to illustrate the role of the oxide layer on the Marangoni convection on the pool surface at elevated temperature. The heavy oxide layer inhibited the fluid flow induced by the Marangoni convection and also became a barrier for the oxygen absorption into the molten weld pool. © 2004 Elsevier B.V. All rights reserved.

http://www.jwri.osaka-u.ac.jp/~dpt9/MSE(2004)O2CO2.pdf

Marangoni convection and weld shape variations in Ar-O2 and Ar-CO2 shielded GTA welding

The purpose of the present work was to investigate the effect of oxide fluxes on weld morphology, arc voltage, mechanical properties, angular distortion and hot cracking susceptibility obtained with TIG welding, which applied to the welding of 5 mm thick austenitic stainless steel plates. A novel variant of the autogenous TIG welding process, oxide powders (Al2O3, Cr2O3, TiO2, SiO2 and CaO) was applied on a type 304 stainless steel through a thin layer of the flux to produce a bead on plate welds. The experimental results indicated that the increase in the penetration is significant with the use of Cr2O3, TiO2, and SiO2. A-TIG welding can increase the weld depth to bead-width ratio, and tends to reduce the angular distortion of the weldment. It was also found that A-TIG welding can increase the retained delta-ferrite content of stainless steel 304 welds and, in consequence, the hot-cracking susceptibility of as-welded is reduced. Physically constricting the plasma column and reducing the anode spot are the possible mechanism for the effect of certain flux on A-TIG penetration.

/pdf/study-of-the-performance-of-stainless-steel-a-tig-welds-5g3rxw8bej.pdf

Study of the Performance of Stainless Steel A-TIG Welds

Creep rupture behaviour of type 316L(N) austenitic stainless steel base metal and its weld joints fabricated both by single-pass activated TIG (A-TIG) and multi-pass conventional TIG (MP-TIG) welding processes were studied at 923 K over a stress range of 160–280 MPa. Both the weld joints possessed lower creep rupture lives than the base metal. The A-TIG weld joint displayed higher rupture lives than the MP-TIG weld joint. Failure in the weld joints occurred in the weld metal. Progressive localization of creep deformation in the weld metal of both the joints led to the premature failure. Accumulation of creep deformation at higher rate was observed in the weld metal of the MP-TIG joint than in the A-TIG joint. Finer microstructural features and higher amount of δ-ferrite was observed in the weld metal of MP-TIG joint than in the A-TIG weld joint. Orientation of the columnar grains and δ-ferrite was nearly transverse to the welding direction in the A-TIG joint, whereas it was towards short transverse to the welding direction in the MP-TIG weld joint. TEM investigation of creep exposed weld metal showed the extensive formation of M 23 C 6 carbides, σ-phase and Laves phase along the boundaries in MP-TIG joint, which were less prevalent in the A-TIG joint. With creep exposure, the δ-ferrite transformed to σ and Laves phases, and creep cavitation was found to be associated with the intermetallic phases. Creep cavitation was more pronounced in the MP-TIG weld joint than in the A-TIG weld joint.

T. Paskell

Papers

GTAW flux increases weld joint penetration