Showing papers by "Andrzej Maziewski published in 2022"
TL;DR: In this article , the existence of weak stripe domains structure was deduced under the consideration of the influence of the Dzyaloshinskii-Moriya interaction on the dynamics of the in-plane magnetized core.
Abstract: Magnetic multilayers of (Ir/Co/Pt)6 with interfacial Dzyaloshinskii-Moriya interaction (IDMI) were deposited by magnetron sputtering with Co thickness d=1.8 nm. Exploiting magneto-optical Kerr effect in longitudinal mode microscopy, magnetic force microscopy, and vibrating sample magnetometry, the magnetic field-driven evolution of domain structures and magnetization hysteresis loops have been studied. The existence of weak stripe domains structure was deduced – tens micrometers size domains with in-plane “core” magnetization modulated by hundred of nanometers domains with out-of-plane magnetization. Micromagnetic simulations interpreted such magnetization distribution. Quantitative evaluation of IDMI was carried out using Brillouin light scattering (BLS) spectroscopy as the difference between Stokes and anti-Stokes peak frequencies Δ f. Due to the additive nature of IDMI, the asymmetric combination of Ir and Pt covers led to large values of effective IDMI energy density Deff. It was found that Stokes and anti-Stokes frequencies as well as Δ f, measured as a function of in-plane applied magnetic field, show hysteresis. These results are explained under the consideration of the influence of IDMI on the dynamics of the in-plane magnetized “core” with weak stripe domains.
4 citations
TL;DR: In this article , the magnetic properties of epitaxial Pt/W(dW)/Co(dCo)/Pt layered films as a function of W (dW) and Co (dCo) layer thicknesses were investigated by means of polar magnetooptical Kerr effect based magnetometry and microscopy as well as Brillouin light scattering (BLS) spectrometry.
3 citations
TL;DR: In this article , the nonlinear regime of photo-induced coherent magnetization dynamics in cobalt-doped yttrium iron garnet films was analyzed both experimentally and numerically.
Abstract: We analyze, both experimentally and numerically, the nonlinear regime of the photo-induced coherent magnetization dynamics in cobalt-doped yttrium iron garnet films. Photo-magnetic excitation with femtosecond laser pulses reveals a strongly nonlinear response of the spin subsystem with a significant increase of the effective Gilbert damping. By varying both laser fluence and the external magnetic field, we show that this nonlinearity originates in the anharmonicity of the magnetic energy landscape. We numerically map the parameter workspace for the nonlinear photo-induced spin dynamics below the photo-magnetic switching threshold. Corroborated by numerical simulations of the Landau-Lifshitz-Gilbert equation, our results highlight the key role of the cubic symmetry of the magnetic subsystem in reaching the nonlinear spin precession regime. These findings expand the fundamental understanding of laser-induced nonlinear spin dynamics as well as facilitate the development of applied photo-magnetism.
1 citations
TL;DR: The magnetic properties of NiO/Co/Pt as a function of Co layer thickness were investigated by polar magneto-optical Kerr effect (PMOKE) and Brillouin Light Scattering (BLS) spectroscopy as discussed by the authors .
Abstract: The magnetic properties of NiO/Co/Pt as a function of Co layer thickness were investigated by polar magneto-optical Kerr effect (PMOKE) (magnetometry and microscopy) and Brillouin Light Scattering (BLS) spectroscopy. PMOKE measurements revealed strong surface anisotropy (1.8 mJ/m2) favoring perpendicular magnetic anisotropy and asymmetric domain wall propagation explained by anticlockwise chirality. BLS measurements show that this chirality is induced by strong interfacial Dzyaloshinskii-Moriya interaction (+ 2.0 pJ/m). This is one of the highest values reported so far for Co layers surrounded by different layers. The observed chirality is opposite to what has been found in Co/oxide interfaces. These results and data published earlier, indicate that the strength of interfacial Dzyaloshinskii-Moriya interaction increases with the amount of stoichiometric NiO. Therefore, this work shows that NiO is the source of the interfacial Dzyaloshinskii-Moriya interaction.