— A modification to Brown and Miller's critical plane approach is proposed to predict multiaxial fatigue life under both in-phase and out-of-phase loading conditions. The components of this modified parameter consist of the maximum shear strain amplitude and the maximum normal stress on the maximum shear strain amplitude plane. Additional cyclic hardening developed during out-of-phase loading is included in the normal stress term. Also, the mathematical formulation of this new parameter is such that variable amplitude loading can be accommodated. Experimental results from tubular specimens made of 1045 HR steel under in-phase and 90° out-of-phase axial-torsional straining using both sinusoidal and trapezoidal wave forms were correlated within a factor of about two employing this approach. Available Inconel 718 axial-torsional data including mean strain histories were also satisfactorily correlated using the aforementioned parameter.

A critical plane approach to multiaxial fatigue damage including out-of-phase loading

Cumulative fatigue damage and life prediction theories: a survey of the state of the art for homogeneous materials

— -A non-linear cumulative fatigue damage model proposed previously is applied to different steels and various loading situations, including two-level tests and block-programs. Its ability to describe all the main features of fatigue damage and the ease of its practical use for engineers are discussed and several examples cited. The relationship with other formulations are pointed out together with the main advantages of the proposed model. A generalization is proposed for both cyclic temperature and multiaxial loading conditions.

A non‐linear continuous fatigue damage model

Mixed mode fatigue crack growth: A literature survey

Multiaxial fatigue: An overview and some approximation models for life estimation

The progressive nature of fatigue damage under multiaxial stress states has been investigated. Experiments were performed on thin-wall tubular specimens of 1045 steel in tension, torsion and combined tension-torsion loading. Two equivalent strain amplitudes, one in the high cycle fatigue (HCF) region and one in low cycle fatigue (LCF) region were employed in this study. Four recently proposed damage theories were evaluated. Crack depth was used as a damage parameter in comparing damage curves under different loading modes.



Different types of crack systems were observed in the HCF and LCF regions. The damage curve obtained in tension loading can be used to evaluate the damage behavior under combined tension—torsion loading. The results of torsion loading show that torsional damage behavior is different from the above two loading modes.

Fatigue damage in 1045 steel under constant amplitude biaxial loading

— The fatigue crack growth behavior of small part-through cracks in 1045 steel and Inconel 718 subjected to biaxial loading has been investigated. Experiments were performed on thin-wall tubular specimens loaded in tension, torsion and combined tension torsion. Crack sizes analyzed ranged from 20 μm to 1 mm and growth rates ranged from 10-7 to 10-4 mm/cycle for 1045 steel and from 10-5 to 10-2 mm/cycle for Inconel. Nucleation and the early growth of cracks occurs on planes of maximum shear strain amplitude for both of these materials even in tensile loading. An equivalent strain based intensity factor was employed to correlate the crack growth rate under mixed mode loading conditions In loading conditions other than torsion, a transition from mode II to mode I was observed for 1045 steel. Principal strains were used to analyze mode I cracks. Cracks in Inconel 718 grow in mode II for the majority of the fatigue life. The maximum shear strain amplitude and the tensile strain normal to the maximum shear strain amplitude plane were used to calculate the strain based intensity factor for mixed mode loading.

Mixed mode small crack growth

— During constant amplitude loading, two different types of crack systems have been reported In the high cycle fatigue (HCF) region, cracks nucleate on a small number of maxium shear strain amplitude planes One of these cracks becomes a dominant crack and leads to failure of the specimen In the low cycle fatigue (LCF) region, equally developed microcracks are observed over the entire gage section and grow during the majority of the life. The failure is due to a linking in which the microcracks join up during the last few cycles of the fatigue life.



To investigate the interaction of these two types of crack systems in biaxial fatigue, experiments were performed on thin-wall tubular specimens in tension, torsion and combined tension-torsion loading The test program included step loading and block loading in which two equivalent strain amplitudes were employed. One of the equivalent strain amplitudes is in the HCF region and the other was in the LCF region



Fatigue lives were predicted from constant amplitude damage curves when a single crack system dominated the fatigue process Two competitive crack systems were sometimes developed on the maximum shear strain amplitude planes in a single specimen under block loading This resulted in a conservative prediction of the fatigue life.

C. T. Hua

Papers

Fatigue damage in 1045 steel under constant amplitude biaxial loading

Mixed mode small crack growth

Fatigue damage in 1045 steel under variable amplitude biaxial loading