This study characterized the mechanical properties (static and under fatigue), the crystalline microstructure (monoclinic - m, tetragonal - t and cubic - c phase contents) and the surface topography of three yttrium-stabilized zirconia (YSZ) materials with different translucent properties, before and after aging in an autoclave (low temperature degradation). Disc-shaped specimens were produced from second generation (Katana ML/HT – high-translucent) and third generations (Katana STML – super-translucent and UTML – ultra-translucent) YSZ ceramics (Kuraray Noritake Dental Inc.), following ISO 6872–2015 guidelines for biaxial flexural strength testing (final dimensions: 15 mm in diameter and 1.2 ± 0.2 mm in thickness), and then subjected to the respective tests and analyses. ML was mainly composed of tetragonal crystals, while STML and UTML presented cubic content. Aging increased the monoclinic content for ML and did not affect STML and UTML. Topographical analysis highlights different grain sizes on the ceramic surface (UTML > STML > ML) and aging had no effect on this outcome. Weibull analysis showed the highest characteristic strength for ML both before and after aging, and statistically similar Weibull moduli for all groups. ML material also obtained the highest survival rates (ML > STML > UTML) for both fatigue strength and number of cycles to failure. All fractures originated from surface defects on the tensile side. Third generation zirconia (Katana STML and UTML) are fully stabilized materials (with tetragonal and cubic crystals), being totally inert to the autoclave aging, and presented lower mechanical properties than the second-generation zirconia (Katana ML - metastable zirconia).

Mechanical reliability, fatigue strength and survival analysis of new polycrystalline translucent zirconia ceramics for monolithic restorations.

Trade-off between fracture resistance and translucency of zirconia and lithium-disilicate glass ceramics for monolithic restorations.

Dental composite and ceramic restorative materials are designed to closely mimic the aesthetics and function of natural tooth tissue, and their longevity in the oral environment depends to a large degree on their fatigue and wear properties. The purpose of this review is to highlight some recent advances in our understanding of fatigue and wear mechanisms, and how they contribute to restoration failures in the complex oral environment. Overall, fatigue and wear processes are found to be closely related, with wear of dental ceramic occlusal surfaces providing initiation sites for fatigue failures, and subsurface fatigue crack propagation driving key wear mechanisms for composites, ceramics, and enamel. Furthermore, both fatigue and wear of composite restorations may be important in enabling secondary caries formation, which is the leading cause of composite restoration failures. Overall, developing a mechanistic description of fatigue, wear, and secondary caries formation, along with understanding the interconnectivity of all three processes, are together seen as essential keys to successfully using in vitro studies to predict in vivo outcomes and develop improved dental restorative materials.

Diana Valladares

Papers

Chairside CAD/CAM materials. Part 3: Cyclic fatigue parameters and lifetime predictions