The nanosized alumina prepared by the hydrolysis method with an average particle size of 20 nm was characterized by X-ray diffraction. The heat capacity measurements of the prepared sample were carried out using an adiabatic calorimeter in the temperature range from 78 to 370 K. Enhancement of heat capacity was observed in the nanostructured materials as the heat capacity data were compared with those of the corresponding coarse-grained materials. The enhanced heat capacity was discussed on the basis of experiments. Differential scanning calorimetry and thermogravimetry were used to determine the thermal stability of the nanostructured alumina.

Enhancement of Molar Heat Capacity of Nanostructured Al2O3

Heat capacities and thermodynamic functions of p-chlorobenzoic acid

Thermodynamic investigation of room temperature ionic liquid: The heat capacity and standard enthalpy of formation of EMIES

A fully automated adiabatic calorimeter controlled on line by a computer used for heat capacity measurements in the temperature range from 80 to 400 K was constructed. The hardware of the calorimetric system consisted of a Data Acquisition/Switch Unit, 34970A Agilent, a 7 1/2 Digit Nano Volt /Micro Ohm Meter, 34420A Agilent, and a P4 computer. The software was developed according to modern controlling theory. The adiabatic calorimeter consisted mainly of a sample cell equipped with a miniature platinum resistance thermometer and an electric heater, two (inner and outer) adiabatic shields, two sets of six junction differential thermocouple piles and a high vacuum can. A Lake Shore 340 Temperature Controller and the two sets of differential thermocouples were used to control the adiabatic conditions between the cell and its surroundings. The reliability of the calorimeter was verified by measuring the heat capacities of synthetic sapphire (α-Al2O3), Standard Reference Material 720. The deviation of the data obtained by this calorimeter from those published by NIST was within ±0.1% in the temperature range from 80 to 400 K.

A fully automated adiabatic calorimeter for heat capacity measurement between 80 and 400 K

A solution-reaction isoperibol calorimeter and standard molar enthalpies of formation of Ln(hq)2Ac (Ln = La, Pr)

A small sample adiabatic calorimeter for measuring heat capacities in the temperature range 60–350 K using the Nernst method has been constructed. The sample cell of the calorimeter is 6 cm3 in the internal volume, equipped with a miniature platinum thermometer and surrounded by two adiabatic shields. Two sets of 6-junction chromel-copel thermocouples were mounted between the cell and the shields to indicate the temperature differences between them. The adiabatic conditions of the cell were automatically controlled by two sets of temperature controller. A mechanical pump was used to pump out the vapour of liquid nitrogen in the cryostat to solidify N2 (1), and 60 K or even lower temperature was obtained. The performance of this apparatus was evaluated by heat capacity measurements on α-alumina. The deviations of experimental results from a smoothed curve lie within ±0.2%, while the inaccuracy is within ±0.5% compared with the recommended reference data in the wole temperature range.

Guanyu Sun

Papers

An adiabatic low-temperature calorimeter for heat capacity measurement of small samples