Electroless nickel, alloy, composite and nano coatings – A critical review

High phosphorus electroless nickel bath has been used to prepare composite coatings containing alumina powders (50 nm, 0.3 μm and 1.0 μm). Deposits were characterized for its structure, morphology and hardness. Incorporation of particle has a marginal influence on the composition. More amount of particle incorporation and uniform distribution was found in composite coatings obtained with 1.0-μm (C3) alumina particles compared to 50-nm (C1) and 0.3-μm (C2) alumina particles. XRD results showed a broad peak of nickel and low intensity alumina peaks present in C3 composite coating in as-plated condition. A marginal improvement in hardness was noticed in as-plated composite coatings. A 15% increase in microhardness was observed in the heat-treated (400 °C for 1 h) composite coatings. Potentiodynamic polarization measurements made on these deposits in 3.5% sodium chloride solution showed that uniform corrosion occurred in C1 and C2 composite coatings whereas localized corrosion was observed in C3 composite coating.

Influence of particle size on the microstructure, hardness and corrosion resistance of electroless Ni–P–Al2O3 composite coatings

The friction and wear of electroless Ni–P matrix with PTFE and/or SiC particles composite

A disk for a hard disk drive is provided. The disk comprises a substrate comprising aluminum, and a coating layer disposed over the substrate. The coating layer comprises an alloy of Ni, X 1 and X 2 , wherein X 1 comprises one or more elements selected from the group consisting of Ag, Au, B, Cr, Cu, Ga, In, Mn, Mo, Nb, Pb, Sb, Se, Sn, Te, W, Zn and Zr, and wherein X 2 comprises either B or P, and wherein X 1 and X 2 do not comprise the same elements.

Electroless coated disks for high temperature applications and methods of making the same

The tribological behaviour of electroless Ni–P–Gr–SiC composite

SUMMARYThe present work pertains to the study of electroless Ni-P and Ni-P-Si3N4 composite coatings. The deposits are obtained from a proprietary high phosphorus electroless nickel plating bath, comprising nickel sulphate, sodium hypophosphite, complexing agents and stabilizers. The maximum weight percent of Si3N4 incorporated in the electroless deposit is obtained at a concentration of 10 g/l in the bath. The electroless Ni-P deposits having 0%, 2.01%, 5.81% and 8.10% of Si3N4, respectively, obtained from baths containing 0, 2, 5 and 10 g/l of Si3N4, are characterized by optical microscopy, XRD and TEM. Hardness is found to increase with the incorporation of Si3N4 at all heat treatment temperatures studied. Also hardness increases with an increase in weight percent of Si3N4 incorporated in the deposit. The analyses of the composite coatings by XRD and TEM reveal that the inclusion of Si3N4 particles does not change the amorphous nature of the Ni-P matrix.

J.N. Balaraju

Papers

Preparation and Characterization of Electroless Ni-P and Ni-P-Si3N4 Composite Coatings