In order to solve the challenge of recyclability of tantalum substrates in high temperature oxidation environments, a novel MoSi2-WSi2-HfSi2-TiSi2 composite ceramic coating containing an Nb interlayer was prepared on the surface of tantalum substrate by a three-step method. The mix ceramic silicide coating exhibited superior performance and effective protection for 10.2 h at 1800 °C, possibly due to the formation of an outer SiO2-HfO2-HfSiO4 composite oxide film with low oxygen permeability, moderate viscosity and thermal expansion coefficient, as well as good self-healing ability. Furthermore, the coating successfully passed 537 thermal cycles from room temperature to 1800 °C. The presence of Nb interlayer significantly mitigated the thermal mismatch between the ceramic coating and the tantalum substrate, and the bidirectional diffusion of Nb element during the high temperature oxidation and thermal shock process further reduced the tendency of the coating to crack. 

Ultra-high temperature oxidation resistance of a novel (Mo, Hf, W, Ti)Si2 ceramic coating with Nb interlayer on Ta substrate

Jian Liu

Papers

Ultra-high temperature oxidation behavior of ZrB2/YSZ modified Si-Mo-W coating with a diffusion barrier on niobium alloy