Nickel Spinel Ferrites: A review

Boosting styrene epoxidation via CoMn2O4 microspheres with unique porous yolk-shell architecture and synergistic intermetallic interaction.

Tunable ferromagnetic resonance linewidth of cobalt-substituted NiCuZn ferrites

Influence of Al3+ substitution on the electrical resistivity and dielectric behavior of Ni0.25Cu0.20Zn0.55AlxFe2-xO4 ferrites synthesized by solid state reaction technique

Interfacial engineering coupling with tailored oxygen vacancies in Co2Mn2O4 spinel hollow nanofiber for catalytic phenol removal

Study of the cation distribution and crystallographic properties of the spinel system NiCrxFe2-xO4 (0.0≤x≤1.0) by neutron diffraction

A series of polycrystalline Ni–Cr ferrites, with the composition NiCr x
 Fe 2−x
 O
 4 (x = 0.0, 0.2, 0.4, 0.6, 0.8, and 1.0), were synthesized by conventional solid state ceramic method. The effect of Cr substitution on the structural, morphological, and magnetic properties of Ni ferrite has been investigated. Formation of single-phase cubic spinel structure of the compositions has been confirmed by X-ray diffraction. The morphological study was performed by scanning electron microscopy, and the average grain size was found to decrease with increasing Cr content. The magnetic properties of the samples were measured using an impedance analyzer and a vibrating sample magnetometer. Saturation magnetization, coercivity, and remanent magnetization have been measured from the hysteresis curves. The value of the saturation magnetization was found to decrease with increasing Cr concentration. The values of coercivity, remanent magnetization, and remanence ratio (M
 r/M
 s) ratio were also reported. The Curie temperatures (T
 c) were determined from the plots of the real part of permeability (
 $\mu _{\mathrm {i}}^{/}$
 ) versus temperature, and the values were found to be 511, 465, 415, 364, and 338 ∘C for x = 0.0, 0.2, 0.4, 0.6, and 0.8, respectively. The frequency dependence of the $\mu _{\mathrm {i}}^{/}$
 , loss factor, and quality factor has been studied as a function of composition in the frequency range 1 kHz–120 MHz. The real part of permeability was observed to be steady up to ∼10 MHz for all the samples. The loss factor (tan δ) of the samples decreased rapidly before 40 kHz and became almost constant with low values after 40 kHz. The values of quality factor have gradually been increased for samples with x ≤ 0.4, whilst the values diminished for samples with x ≥ 0.6.