TL;DR: In this article, the properties of prealloyed Fe-1·5Mo base powder with and without additions of elemental Si, ferrosilicon, and carbon under various process conditions have been investigated.
Abstract: Alpha phase sintering, sinter hardening, and mechanical properties of prealloyed Fe-1·5Mo base powder with and without additions of elemental Si, ferrosilicon, and carbon under various process conditions have been investigated. Liquid paraffin, as a new lubricating agent, was found to be useful in reducing segregation, interparticle and die wall frictions, as well as reducing ejection forces and die and tool wear. It was found that addition of Si to the base powder enhanced the sintering process by stabilisation of the α-phase and formation of two kinds of liquid phase at ~1045 and ~1180°C, corresponding to the solidus and liquidus temperatures, respectively. This addition increased the tensile strength of the as sintered Fe-1·5Mo from 174 to 445MPa owing to massive solid solution strengthening effect of Si. An optimum sinter hardenable alloy, of composition Fe-1·5Mo + 3Si + 1·2C, provided a high sintered density of 7·55g cm-3, tensile and bend strengths of7 64 and 1405MPa, respectively, with 2·5%...
8 citations