Showing papers by "Miroslav Karlík published in 2010"

TL;DR: In this paper, Spark Plasma Sintering (SPS) was employed to produce specimens from gas atomized Fe-43at.%Al powder sieved into different size fractions.

TL;DR: Fracture experiments performed at room temperature on four test samples made of Fe-3wt.%Si single crystals with an edge crack (1/1/0) showed approximately 45° deflections of the crack from the initial crack plane (1 /1 /0), which appeared to be independent on loading rate as mentioned in this paper.

TL;DR: In this paper, FeAl-based coatings were deposited on low carbon steel using two different plasma spraying technologies, gas stabilized plasma gun (GSP) and water stabilized plasminar gun (WSP), resulting in different deposition conditions.