Showing papers by "Naoyuki Hashimoto published in 1993"
TL;DR: In this article, a Fe-Cr-Ni model alloy was irradiated using a high voltage electron microscopy (1000 kV), and in-situ observations on structural evolution and microchemical analyses were carried out.
Abstract: A Fe-Cr-Ni model alloy was electron-irradiated using a high voltage electron microscopy (1000 kV), and in-situ observations on structural evolution and microchemical analyses were carried out. When the Fe-Cr-Ni alloy was irradiated, the nucleations of dislocation loops followed by voids were observed and at the same time when a grain boundary migration occurred. The compositional analysis after irradiation of an area including a grain boundary indicated nickel enrichment and chromium depletion near the grain boundary. It is suggested that when the radiation-induced point defects flow into the grain boundary, boundary migration and solutes redistribution are induced and the magnitudes depend on net point defects flow, especially that of interstitial atoms
27 citations