Showing papers by "Pedro José Sánchez-Soto published in 2009"
••
TL;DR: In this article, the results are presented for the chemical characterization carried out with 53 raw material samples with phyllosilicates from outcrops located between the provinces of Almeria and Granada (Spain) in order to use them as waterproof layers under the floors of greenhouses.
Abstract: The results are presented for the chemical characterization carried out with 53 raw material samples with phyllosilicates from outcrops located between the provinces of Almeria and Granada (SE Spain) in order to use them as waterproof layers under the floors of greenhouses. For this purpose, the samples have been studied by these techniques: X-Ray Diffraction (XRD), X-Ray Fluorescence (WDXRF), Scanning Electron Microscopy (SEM), chemical analysis by energy-dispersive X-Ray detection (EDX), and thermogravimetry. To isolate groups of phyllite samples with similar chemical profiles and correlations between the samples, the WDXRF data (11 chemical elements) have been processed using the methodology of exploratory multivariate statistical analyses: cluster analysis, main-component analysis, and discriminating canon analysis. This study was performed as a screening test and as a means of finding similarities and correlations among all 53 phyllite samples, allowing the isolation of groups of phyllite samples with similar chemical profiles. The results indicate that the 53 phyllite samples can be divided into two main groups. The first group is subdivided into two subgroups (1 and 2), one of which includes most of the samples. The latter is further classified into three blocks with the same chemical composition. This allows to search for the raw material with potentially the best waterproof characteristics within the five groups. The classification is of validity as a screening test for subsequent experimental determinations concerning the physical properties of these samples. Copyright © 2009 John Wiley & Sons, Ltd.
15 citations
•
TL;DR: In this article, aplicación de un sistema de informacion geografica (SIG) como herramienta eficaz a la hora de abordar several fases of investigacion sobre materias primas de interes for el sector of la Ceramica and el Vidrio, with two ejemplos: prospeccion and caracterización of materias, utilizadas as material impermeabilizante ademas de potencial interess ceram
Abstract: En este trabajo se muestra la aplicacion de un sistema de informacion geografica (SIG) como herramienta eficaz a la hora de abordar
varias fases de investigacion sobre materias primas de interes para el sector de la Ceramica y el Vidrio, con dos ejemplos: prospeccion
y caracterizacion de materias primas, utilizadas como material impermeabilizante ademas de potencial interes ceramico y estudio
de canteras de extraccion de caliza y marmol. Para ello, se han diferenciado tres fases en el trabajo: construccion de la base de datos
cartografica, fusion de las bases de datos y depuracion; finalmente, se realiza el desarrollo de la aplicacion.
De este estudio se concluye que el SIG se convierte en una herramienta viva, a la que se le pueden ir incorporando nuevos datos, como
son puntos de muestreo, resultados de ensayos y determinaciones realizadas con las muestras, nuevas vias y caminos, empresas que
poseen la concesion, etc., como ha quedado expuesto con los ejemplos descritos. Todo ello permite una explotacion mucho mas
racional y eficiente desde los puntos de vista tecnico, medioambiental y economico. Se deduce un claro interes del metodo de trabajo
propuesto con utilidad para investigadores, tecnologos y empresarios del ambito que se ocupan de la valorizacion de materias
primas de aplicacion en el procesamiento de materiales de este sector.
6 citations
•
TL;DR: In this paper, the efecto of tratamiento mecanico por molienda in seco, empleando un molino de bolas, en the texturales de pirofilita, was investigated.
Abstract: Se ha investigado el efecto del tratamiento mecanico por molienda en seco, empleando un molino de bolas, en las
propiedades texturales de pirofilita. Las isotermas de adsorcion-desorcion de gas nitrogeno a -195 oC, determinadas en el
material original y modificado por molienda, no han mostrado fenomenos de histeresis pronunciados. Se ha encontrado
que los volumenes de gas adsorbidos aumentan de forma gradual al incrementarse el tiempo de molienda, presentando
un maximo a los 30 minutos. A partir de este tiempo de tratamiento, aquellos disminuyen hasta llegar a una situacion
muy similar a la inicial. La evolucion de los valores de superficie especifica (SBET), determinados mediante aplicacion de
la ecuacion BET, ha permitido apreciar un rapido incremento al aumentar el tiempo de molienda desde 2 m2xg-1 en la
muestra original hasta un maximo de 60 m2xg-1 a los 30 minutos, llegando a un valor de 7.5 m2xg-1 a los 325 minutos. Este
comportamiento se atribuyo a una disminucion del tamano de las particulas del silicato laminar por efecto de la molienda
hasta un limite. Por encima de este limite, las particulas comienzan a reagregarse y aglomerarse mediante un proceso
mecanoquimico de soldadura en frio, originado por una alta reactividad superficial y, en consecuencia, disminuyen
progresivamente los valores de SBET lo que coincide con el mayor grado de alteracion estructural que se produce en el
material y la amorfizacion consiguiente.
Asimismo, del estudio textural realizado se ha mostrado la ausencia de microporos en el proceso de fisisorcion del gas
nitrogeno por los materiales modificados debido al efecto de la molienda, deduciendose que dicho proceso se produce
en multicapas. Una estimacion de la distribucion de tamano de los poros formados con el tratamiento de molienda ha
indicado una contribucion de los tamanos comprendidos entre 20 y 50 A al aumento de SBET. Por encima de 30 minutos de
molienda esta contribucion disminuye progresivamente al producirse el proceso de reagregacion de las particulas y, en
particular, con una contribucion importante de los poros de diametros inferiores a 40 A.
4 citations
01 Nov 2009
TL;DR: In this article, a wide investigation on processing of mullite and mullite-based ceramic composites from Al metal wastes and waste by-products of mining tin ores with high kaolinite content is presented.
Abstract: The present work is part of a wide investigation on processing of mullite and mullite-based ceramic composites from Al metal wastes and waste by-products of mining tin ores with high kaolinite content. The Al wastes were dissolved in acid solution, mixed with aqueous suspension of kaolinite and precipitated the oxy-hydroxide using two alkaline bases. Kaolinite and α-alumina mixtures were also used to compare the results. Porous mullite and mullite-based composites (52-45 vol %) can be obtained by firing some precursors at 1500-1600 oC for 120-30 min. They have interesting potential applications, such as ceramic substrates, refractories, filters and thermal barriers. The method has implications for the recovery and recycling of Al wastes, besides the application of waste by-products of mining as valuable raw ceramic materials.
3 citations