Zn1–xCoxO (x = 0, 0.05, 0.10, and 0.15) nanoparticles (NPs) were synthesized by a coprecipitation method. The crystalline sizes of synthesized samples were calculated from the powder XRD patterns, which were found to decrease with the increase of cobalt content. The FT-IR spectra confirmed the Zn–O stretching bands at 468, 456, 452, and 461 cm–1 for the respective ZnO NPs. SEM images demonstrated the distinct flowerlike morphology. The photoluminescence spectra of all the samples exhibited a broad emission in the visible range. XPS studies were carried out for Zn0.90Co0.10O NPs. The carriers (donors) bound on the Co sites were observed from the micro-Raman spectroscopic studies. The pure and Co-doped ZnO NPs showed significant changes in the M–H loop where the diamagnetic behavior of ZnO changes to ferromagnetic nature when doping with Co. Oxygen vacancies and zinc interstitials were found to be the main reasons for room-temperature ferromagnetism in the Co-doped ZnO NPs with the support of the results ob...

Effect of Cobalt Doping on Structural, Optical, and Magnetic Properties of ZnO Nanoparticles Synthesized by Coprecipitation Method

Pure ZnO and Neodymium (Nd) doped ZnO nanoparticles (NPs) were synthesized by the co-precipitation method. The synthesized nanoparticles retained the wurtzite hexagonal structure. From FESEM studies, ZnO and Nd doped ZnO NPs showed nanorod and nanoflower like morphology respectively. The FT-IR spectra confirmed the Zn-O stretching bands at 422 and 451 cm−1 for ZnO and Nd doped ZnO NPs respectively. From the UV-VIS spectroscopic measurement, the excitonic peaks were found around 373 nm and 380 nm for the respective samples. The photoluminescence measurements revealed that the broad emission was composed of ten different bands due to zinc vacancies, oxygen vacancies and surface defects. The antibacterial studies performed against extended spectrum β-lactamases (ESBLs) producing strains of Escherichia coli and Klebsiella pneumoniae showed that the Nd doped ZnO NPs possessed a greater antibacterial effect than the pure ZnO NPs. From confocal laser scanning microscopic (CLSM) analysis, the apoptotic nature of the cells was confirmed by the cell shrinkage, disorganization of cell wall and cell membrane and dead cell of the bacteria. SEM analysis revealed the existence of bacterial loss of viability due to an impairment of cell membrane integrity, which was highly consistent with the damage of cell walls.

/pdf/in-vitro-antibacterial-activity-of-zno-and-nd-doped-zno-lz9ybaivd7.pdf

In vitro antibacterial activity of ZnO and Nd doped ZnO nanoparticles against ESBL producing Escherichia coli and Klebsiella pneumoniae.

A hierarchical nano- and microstructured morphology for visible-blind UV photo-detectors is developed, which provides record-high milliampere photocurrents, nanoampere dark currents, and excellent selectivity to ultralow UV light intensities. This is a significant step toward the integration of high-performance UV photodetectors in wearable devices.

/pdf/ultraporous-electron-depleted-zno-nanoparticle-networks-for-13ccc7udfh.pdf

Ultraporous Electron‐Depleted ZnO Nanoparticle Networks for Highly Sensitive Portable Visible‐Blind UV Photodetectors

Pure and copper-doped zinc oxide nanoparticles (NPs) have been synthesized via chemical co-precipitation method where hydrazine is used as reducing agent and aqueous extract of Euphorbia milii plant as capping agent. Main objectives of the reported work are to investigate the effect of copper doping on crystal structure of ZnO nanoparticles; to study the effect of copper doping on optical band gap of ZnO nanoparticles and photoluminescence (PL) study of pure and copper-doped ZnO nanoparticles. To achieve the aforementioned objectives, XRD and SEM tests were performed for the identification and confirmation of crystal structure and morphology of the prepared samples. From XRD data the average grain size for pure ZnO was observed to be 24.62 nm which was first decreased to 18.95 nm for 5 wt% Cu-doped sample and then it was found to increase up to 37.80 nm as the Cu doping was increased to 7 wt%. Optical band gap of pure and Cu-doped ZnO nanoparticles was calculated from diffuse reflectance spectroscopy (DRS) spectra and was found to decrease from 3.13 eV to 2.94 eV as the amount of Cu increases up to 7 wt%. In photoluminescence study, PL technique was used and enhanced visible spectrum was observed. For further characterization FT-IR and EDX tests were also carried out.

Structural and optical properties of pure and copper doped zinc oxide nanoparticles

Photocatalytic degradation of aqueous solution of methylene blue dye under UV light illumination was studied by using manganese doped ZnO ( Z n 1 - x M n x O , where x = 0.00 , x = 0.02 a n d x = 0.05 ) nanoparticles as a photocatalyst. The nanophotocatalysts were synthesized by wet chemical co-precipitation method. The structural, morphological, and optical properties of the photocatalysts were done by X-ray diffraction (XRD), Scanning Electron microscope (SEM), Energy Dispersive X-Ray (EDX), photoluminescence (PL), Fourier Transform Infrared Ray (FTIR) and UV–visible spectroscopic techniques. An improved photocatalytic efficiency of ZnO was observed upon doping with Mn and 2% Mn-doped ZnO exhibited the highest photocatalytic activity among the doped samples. The effect of operating parameters such as amount of catalyst, the initial dye concentration, and initial pH on the rate of dye degradation using 2% Mn-doped ZnO was studied. Under the optimum operation conditions, approximately 99% of dye removal was achieved after 120 min of irradiation.

S. Muthukumaran

Papers

Structural, FTIR and photoluminescence studies of Cu doped ZnO nanopowders by co-precipitation method