Showing papers by "Saurin Majumdar published in 2006"
TL;DR: In this article, the authors show that the threshold stress is approximately 75-80 MPa for both nonirradiated and high-burnup stress-relieved Zry-4 fuel cladding cooled from 400°C and, under ring compression at both room temperature and 150°C, that radial-hydride precipitation embrittles Zry4.
Abstract: Prestorage drying operations of high-burnup fuel may make Zircaloy-4 (Zry-4) fuel cladding more susceptible to failure, especially during fuel handling, transport, and post-storage retrieval. In particular, hydride precipitates may reorient from the circumferential to the radial direction of the cladding during drying operations if a threshold level of hoop stress at or above a corresponding threshold temperature is exceeded. This study indicates that the threshold stress is approximately 75–80 MPa for both nonirradiated and high-burnup stress-relieved Zry-4 fuel cladding cooled from 400°C and, under ring compression at both room temperature and 150°C, that radial-hydride precipitation embrittles Zry-4. Specifically, the plastic tensile hoop strain needed to initiate unstable crack propagation along radial hydrides decreases dramatically from >8% to lt;1% as radial-hydride fraction increases. Lower hydrogen contents (lr;300wppm) appear to be more susceptible to radial-hydride embrittlement compared to hig...
83 citations