Shunji Hiwatari is an academic researcher. The author has contributed to research in topics: Ferrite (iron) & Austenite. The author has an hindex of 12, co-authored 36 publications receiving 407 citations.
Papers
More filters
Patent
High strength hot dip galvannealed steel sheet good in workability and its production
TL;DR: In this paper, a hot dip galvanized steel sheet is composed of C, Si, Mn, P, S, Al and N. The problem of improving tensile strength and press workability of a steel sheet by specifying the contents of C and Si, and specifying the relation between the amounts of Si and C, and between the amount of Cr and Mn to be added is solved.
Patent
Steel sheet for press forming with excellent ductility after forming, its forming method and automotive parts using the steel sheet for press forming
Masashi Azuma,Shunji Hiwatari,Kosaku Shioda,Shigeru Yonemura,Naoki Yoshinaga,直樹 吉永,昌史 東,俊二 樋渡,浩作 潮田,繁 米村 +9 more
TL;DR: In this article, a steel sheet which has a composition consisting of, by mass, 0.1 to 0.4%, 0.001 to 3.0%, 1.5 to 4.0% Si, 1.1% P, ≤0.05% S, 0,005 to 0,1% Al, ≤ 0.01% N and the balance Fe with inevitable impurities was heated at 1 to 100°C/sec heating rate, held in a temperature region of 700 to 850°C for 10 to 6,000 sec and then press formed in a
Patent
High yield ratio and high strength cold-rolled steel plate and high yield ratio and high strength galvanized steel plate excellent in weldability and ductility, and high yield ratio and high strength alloyed galvanized steel plate and its manufacturing method
TL;DR: In this paper, the authors proposed a high yield ratio and high strength hot-rolled steel plate having excellent weldability and ductility is a steel containing, by mass%, over 0.68 or more and less than 0.0040 of B and the balance of iron and inevitable impurities.
Patent
High young's modulus steel plate, hot dip galvanized steel sheet using the same, hot dip galvannealed steel sheet, high young's modulus steel pipe, high young's modulus hot dip galvanized steel pipe, high young's modulus hot dip galvannealed steel pipe, and method for production thereof
Koji Hanya,Shunji Hiwatari,Akihiro Miyasaka,Takehide Senuma,Ryoichi Sugano,Natsuko Sugiura,Manabu Takahashi,Nobuyoshi Uno,Naoki Yoshinaga,公司 半谷,直樹 吉永,暢芳 宇野,明博 宮坂,夏子 杉浦,俊二 樋渡,武秀 瀬沼,良一 菅野,学 高橋 +17 more
TL;DR: In this article, an embodiment of a high Young's modulus steel sheet, wherein it has a chemical composition comprising, by mass, C: 0.0005 to 0.30%, Si: 2.5% or less, Mn:0.1 to 5.0%, P: 0,015 to 1.5%, Nb: 0., 0.005 to 0., and Ti: 48/14×N (mass%) to 0,
Patent
High-strength steel sheet, high-strength galvanized steel sheet and high-strength galvannealed steel sheet having excellent stretch-flanging property and impact resistance, and production method therefor
TL;DR: In this article, the authors proposed a method to provide a high-strength steel sheet, a high strength galvanized steel sheet and a highstrength galvannealed steel sheet in a class of 440 to 780 MPa which have excellent strength-flanging properties and impact resistance, and provide a production method therefor.