Showing papers by "Wasi Khan published in 2023"

Physical properties and photocatalytic activity of Cr doped TiO2 nanoparticles.

Abstract: Nanocrystalline Ti1-x Crx O2 (0≤ x ≤0.20) samples are synthesized via acid-modified sol-gel process and characterized with various techniques, such as HRTEM, FESEM, Raman, XPS, DTA and VSM. The TEM image of TiO2 exhibits elongated nanoparticles with an average size of 10 nm. The HRTEM in combination with selected area electron diffraction (SAED) patterns reveals the interplanar spacing and polycrystalline nature of the samples, respectively. FESEM micrographs reveal non-uniform morphologies and less aggregation of the particles in the doped sample. Raman spectra ensure the phase purity of the samples and a blue shift on Cr doping. X-ray photoelectron spectra (XPS) predict the chemical state of the elements and oxygen vacancies in the prepared samples. The room temperature magnetic studies reveal a significant variation in the magnetic parameters on Cr doping in TiO2 . The differential thermal analysis (DTA) shows the structural phase transition at ∼630°C. The photocatalytic performance is studied for the degradation of methylene blue (MB) dye under visible-light irradiation. A higher photocatalytic efficiency is found for the 20% of Cr-doped TiO2 . These studies propose that the appropriate incorporation of Cr ions makes TiO2 very efficient for visible light-driven photocatalysts required for applications in wastewater treatment. In the present study, nanoparticles of TiO2 and Cr doped TiO2 by a cost-effective acid-modified sol-gel process. The effect of Cr doping on the microstructure, thermal, magnetic and photocatalytic properties of TiO2 were explored in detail. The transmission electron microscopy (TEM) images exhibit the presence of elongated nanoparticles with an average size of 10 nm. Field emission scanning electron microscopy (FESEM) was used to study the surface morphology of the synthesized materials, which revealed non-uniform morphologies and less aggregation of the particles in the Cr-doped sample. Energy dispersive x-ray spectroscopy (EDS) confirms the elemental compositions with the appropriate stoichiometry of the elements. Raman spectra ensure the phase purity of the materials and also a blue shift with the incorporation of Cr ions in TiO2 . X-ray photoelectron spectra (XPS) predict the chemical state of the elements and oxygen vacancies in the prepared samples. The magnetic nature of all the synthesized samples was examined through the vibrating sample magnetometer (VSM) and revealed weak ferromagnetic behavior of the samples. These results signify that the oxygen vacancies and defects play a crucial role in developing the ferromagnetic nature of oxide semiconductors. The differential thermal analysis (DTA) shows the structural phase transition at ∼630°C. The photocatalytic performance of the prepared samples was studied for the degradation of methylene blue (MB) dye under irradiation of visible light. A higher photocatalytic efficiency was found for the 20% of Cr-doped TiO2 . These studies propose that the appropriate incorporation of Cr ions makes TiO2 very efficient for visible light-driven photocatalysts required for applications in wastewater treatment. This article is protected by copyright. All rights reserved.