Xiao-Fen Li is an academic researcher from Texas Center for Superconductivity. The author has contributed to research in topics: Electromagnetic coil & Magnetic field. The author has an hindex of 8, co-authored 22 publications receiving 155 citations. Previous affiliations of Xiao-Fen Li include University of Houston & Shanghai Jiao Tong University.
Papers
More filters
Journal ArticleDOI
Control of in-field performance of 25 mol.% Zr-added REBCO superconductor tapes
M. Heydari Gharahcheshmeh,M. Heydari Gharahcheshmeh,Goran Majkic,Eduard Galstyan,Aixia Xu,Y. Zhang,Xiao-Fen Li,Venkat Selvamanickam +7 more
TL;DR: In this paper, the relation between the c-axis lattice parameter of REBa2Cu3O7−δ (REBCO and RE = Gd, Y) superconductors with 25.5% Zr addition and the critical current density (Jc) was determined at (77 K, 0 ǫT), (30‚K, 3ǫt (B||c)), and (30´K, 9ǫǫ)
Journal ArticleDOI
Fabrication and Electromagnetic Characterization of Ultrasmall Diameter REBCO Wires
TL;DR: Using ultrathin RE-Ba-Cu-O (REBCO, RE = rare earth) superconductor tapes, a multilayer round wire with an outer diameter of 1.6 mm on a flexible copper former of 0.8 mm diameter was fabricated.
Journal ArticleDOI
Symmetric tape round REBCO wire with J e (4.2 K, 15 T) beyond 450 A mm−2 at 15 mm bend radius: a viable candidate for future compact accelerator magnet applications
Soumen Kar,Soumen Kar,Wenbo Luo,Anis Ben Yahia,Xiao-Fen Li,Goran Majkic,Venkat Selvamanickam +6 more
TL;DR: In this paper, a 1.6 mm diameter symmetric tape round (STAR) wire made with six 2.5 mm wide symmetric tapes reached an engineering current density (J e) of 454 A mm−2 at 4.2 K in a background field of 15 T at a bend radius of 15 mm.
Journal ArticleDOI
Superconducting transition width (ΔT c) characteristics of 25 mol% Zr-added (Gd, Y)Ba2Cu3O7−δ superconductor tapes with high in-field critical current density at 30 K
M. Heydari Gharahcheshmeh,Eduard Galstyan,Aixia Xu,J. Kukunuru,R. Katta,Y. Zhang,Goran Majkic,Xiao-Fen Li,Venkat Selvamanickam +8 more
TL;DR: In this article, the superconducting transition width (∆T c) characteristics of REBa2Cu3O7−δ (REBCO and RE = Gd, Y) superconductor tapes with Zr content of 25 mol% with high lift factor has been determined.
Journal ArticleDOI
MOCVD of Heavily-Doped 25 mol.% Zr-Added (Gd, Y)Ba2Cu3O7-δ Coated Conductors
Meysam Heydari Gharahcheshmeh,Eduard Galstyan,Jaideep Kukunuru,Rahul Katta,Goran Majkic,Xiao-Fen Li,Venkat Selvamanickam +6 more
TL;DR: In this paper, the effects of deposition temperature and oxygen partial pressure on the microstructure and the texture of (Gd, Y)Ba2Cu3O7-δ coated conductors with Zr content of 25 mol.