Showing papers in "Plating and Surface Finishing in 1984"

Operation and use of sodium-borohydride-reduced electroless nickel

Abstract: Ces revetements ont un durete, une resistance a l'usure et un pouvoir lubrifiant superieurs a ceux des revetements reduits par d'autres composes du bore. Leur emploi est cependant limite par leur cout eleve et la complexite du fonctionnement du bain

Historical highlights of electroless plating

Abstract: Cas de Ni-P; Cu; de composites (particules dans bains pour depots de Ni-P); semiconducteurs

A cobalt/chromic oxide composite coating for high-tempereture wear resistance

Abstract: Un composite contenant 20 a 25% en poids de Cr 2 O 3 dans une matrice de cobalt presente une excellente resistance a l'usure adhesive a des temperatures de 300 a 700°C, en raison de la formation dans l'air d'une couche d'oxyde orientee de Co 3 O 4 . Ce depot est beaucoup plus resistant a l'usure a haute temperature que les revetements de Ni/TiC ou Ni-P/SiC

Corrosion resistance of electroless deposits for electromagnetic interference shielding

Abstract: Evaluation de l'aptitude a la protection contre le brouillage des revetements chimiques de nickel, de cuivre et des revetements composites, avant et apres essais de corrosion acceleree. Lorsque le depot chimique de nickel contient au moins 6% de phosphore, des revetements composites de nickel chimique (0,5 μm) sur cuivre chimique (0,5 μm) presentent une efficacite de protection meilleure apres corrosion que les revetements simples

Determination of chloride and sulfate in chromic acid by ion chromatography

Abstract: Les proprietes chromatographiques de ces ions etant affectees par de grandes concentrations de chromate et par l'acidite de l'echantillon, les donnees d'etalonnage des echantillons normalises de chlorure et de sulfate doivent etre obtenues en utilisant la concentration de l'acide chromique de l'echantillon. Si on doit analyser le chromate de potassium, l'echantillon normalise doit etre prepare dans le chromate de potassium

Effect of metal ion depletion on cobalt-hardened gold

Abstract: Etude par microscopes electroniques a balayage et en transmission, de l'influence de l'usage du bain sur la microstructure et la ductilite de depots electrolytiques d'or durci au cobalt. Lorsque le bain est usage, la ductilite diminue, ce qui semble du a la difference de densite des inclusions de polymere et aux bulles d'hydrogene

Effect of Methanol and Formic Acid on Chromium Plating

Abstract: : Since 1856 many plating baths have been proposed for chromium electrodeposition. The most successful of these are chromic acid baths containing sulfate catalysts or sulfate and silicofluoride. The current efficiency of these baths ranges from about 10 to 25 percent, depending on the catalyst and plating conditions. Often Cr3+ is considered detrimental to the functioning of the bath. Trivalent chromium is produced at the cathode during plating and can be oxidized to Cr6+ at the anode under proper conditions. The current efficiency for the Cr3+ production at the cathode depends on the temperature, current density, and catalyst concentration. This paper reports the effects of methanol, formic acid, iron, and Cr3+ on the current efficiency and on the appearance of the deposit. Under certain conditions these additives appear to be beneficial. Reprint. Keywords: Methanol; Formic acid; Chromium; Chromic acid; Chromium alloys; Electrodeposition.

The hardness of iron electrodeposited with ultrasound

Abstract: Influence de l'agitation par ultrason sur six solutions de placage. Les depots obtenus ont une microdurete plus grande que ceux qui sont obtenus dans des bains agites mecaniquement. La porosite et la corrosion par piqures ont tendance a etre moindres

An electrochemical cell for cadmium recovery and recycling

Abstract: Cellule electrochimique contenant un lit fluidise de perles de verre ameliorant le depot cathodique sous forme de metal pur du cadmium entraine dans les eaux de rincage des installations de cadmiage

A high-speed nitric acid strip solution for electroless nickel

Abstract: Nouvelle solution contenant 1,2% de H 2 O 2 et 21% de HNO 3 , moins dangereux pour le personnel et l'equipement que la solution habituelle a 35% de HNO 3 . Description d'experiences en laboratoire et dans l'industrie

Design of a new electroplating laboratory

Abstract: On expose la philosophie de la conception, la disposition physique des elements, l'appareillage et les possibilites d'un laboratoire bien equipe

Study of sulfonates in Watts nickel plating baths

Abstract: Effet du 2-butyne-1,4 diol et de sulfonates solubles. Etude de la brillance et des contraintes internes du depot

Plating functional chromium at high efficiency with no cathodic etching

Abstract: Nouveau procede pour lequel l'efficacite de la cathode est ≥40%. La nouvelle solution ne cause pas d'attaque significative a faible densite de courant. Le chrome peut etre depose a environ 125 μm/h, et on realise des economies d'energie

Copper recovery from dilute solutions using a barrel planter

Abstract: La recuperation du cuivre est maximale lorsque le volume de travail est de 50 a 70% de la capacite totale. Comparaison avec les performances d'un reacteur electrochimique a lit fixe