Electrochemical Conditions at the Tip of an Advancing Stress Corrosion Crack in AISI 4340 Steel
Reads0
Chats0
TLDR
Stress corrosion cracking in AISI 4340 steel was studied utilizing an Sb/Sb2O3 Ag/AgCl probe which simultaneously measured the crack tip electropotential and the electrolyte pH of the regi...Abstract:
Stress corrosion cracking in AISI 4340 steel was studied utilizing an Sb/Sb2O3 Ag/AgCl probe which simultaneously measures the crack tip electropotential and the electrolyte pH of the regi...read more
Citations
More filters
Journal ArticleDOI
A new model for hydrogen-assisted cracking (hydrogen “embrittlement”)
TL;DR: A new model for hydrogen-assisted cracking is presented in this article, which explains the observations of decreasing microscopic plasticity and changes of fracture modes with decreasing stress intensities at crack tips during stress-corrosion cracking and HAC of quenched-and tempered steels.
Journal ArticleDOI
Passivity breakdown, pit initiation and propagation of pits in metallic materials – Review
TL;DR: In this article, the authors present a review of literature which covers aspects of pitting corrosion observed in metallic materials, focussing on events associated with nucleation of pits, i.e. passivity breakdown, initiation of pits and their propagation stage.
Hydrogen Assisted Cracking of High Strength Alloys
TL;DR: In this paper, a plot of plane strain fracture toughness vs. tensile yield strength for ultra-high strength steels (UHSS) and beta-Ti alloys precipitation hardened with a phase is presented.
Journal ArticleDOI
Tafel’s law in pitting corrosion and crevice corrosion susceptibility
TL;DR: In this article, the critical potentials for pitting are reviewed under the scope of their relation with the crevice corrosion mechanism and a short review of the correlation between pitting corrosion and Tafel's law is made.
Related Papers (5)
Methods for Studying the Solution Chemistry Within Stress Corrosion Cracks
On the Mechanism of Localized Corrosion of Iron and Stainless Steel I . Electrochemical Studies
The use of current/voltage curves for the study of localized corrosion and passivity breakdown on stainless steels in chloride media
B.E. Wilde,E. Williams +1 more