Collapse modes in aluminium honeycomb sandwich panels under bending and impact loading

The work describes the manufacturing and testing of graded conventional/auxetic honeycomb cores. The graded honeycombs are manufactured using Kevlar woven fabric/914 epoxy prepreg using Kirigami techniques, which consist in a combination of Origami and ply-cut processes. The cores are used to manufacture sandwich panels for flatwise compression and edgewise loading. The compressive modulus and compressive strength of stabilized (sandwich) honeycombs are found to be higher than those of bare honeycombs, and with density-averaged properties enhanced compared to other sandwich panels offered in the market place. The modulus and strength of graded sandwich panel under quasi-static edgewise loading vary with different failure mode mechanisms, and offer also improvements towards available panels from open literature. Edgewise impact loading shows a strong directionality of the mechanical response. When the indenter impacts the auxetic portion of the graded core, the strong localization of the damage due to the negative Poisson’s ratio effect contains significantly the maximum dynamic displacement of the sandwich panel.

Graded conventional-auxetic Kirigami sandwich structures: Flatwise compression and edgewise loading

Experimental and numerical study on honeycomb sandwich panels under bending and in-panel compression

Nature has provided us with extraordinary resources to tackle design challenges facing in modern society nowadays. The multistate structures inspired by animal shell have proven effective to improve the impact resistance of composite laminate. This study aims to identify the crash responses and crashworthiness characteristics of bio-inspired sandwich structures composed of carbon fiber reinforced plastic (CFRP) panels and aluminum honeycomb. The crash responses, failure mode as well as the effects of core side length, height and impact velocity on peak load and energy absorption were explored herein. The differences of crashworthiness characteristics between the CFRP aluminum honeycomb sandwiches and bare CFRP panel were quantified. Two typical load-displacement relations, namely single-peak and double-hump curves, were observed in the tests. It was noted in the energy-displacement curve, where the slopes corresponding to the failure stages of the upper and lower face-sheets, were greater than that in the honeycomb failure stage, indicating that the bare aluminum honeycomb was of lower energy absorption capacity than the CFRP face-sheet. By comparison, the honeycomb filling was an effective way to improve the impact resistance of CFRP structure, yielding higher energy absorption and lower peak load during the impact. It was also found that the crashworthiness characteristics were more sensitive to the core length than to the core height; and the specific energy absorption (SEA) varied insignificantly with the increase in the core height. It was noted that the peak load, absorbed energy and SEA increased significantly under high impact velocity.

Dynamic crash responses of bio-inspired aluminum honeycomb sandwich structures with CFRP panels

Behaviour of sandwich panels subjected to intense air blast - Part 1: Experiments

Aluminum sandwich construction has been recognized as a promising concept for structural design of lightweight transportation systems such as aircraft, high-speed trains and fast ships. The aim of the present study is to investigate the strength characteristics of aluminum sandwich panels with aluminum honeycomb core theoretically and experimentally. A series of strength tests are carried out on aluminum honeycomb-cored sandwich panel specimen in three point bending, axial compression and lateral crushing loads. Simplified theories are applied to analyze bending deformation, buckling/ultimate strength and crushing strength of honeycomb sandwich panels subject to the corresponding load component. The structural failure characteristics of aluminum sandwich panels are discussed. The test data developed are documented.

Gyu Sung Kim

Papers

The strength characteristics of aluminum honeycomb sandwich panels