SHS/QP is an efficient method for preparing FGM. But in synthesis process, high temperature and high velocity may result in some results not expected by us, which as a consequence will affect the FGM’s performance. A1 so, repeatability of the concentration distribution is not good.

In this work, FGMs were prepared by SHS/QP and heat treating, which had very thin gradient layer and wide range concentration distribution. The manufacturing was carried out as following: the pellet including mixture-metal layers was processed by SHS/QP, and then the product was treated longer than two hours at 700 °C ~ 1200 °C. Quantitative and qualitative analyses were carried out to different points in the gradient layer. The result indicates that the thickness of the gradient layer is decided by the heat treatment to a great extent. The chemical and phase composition, and the connection between grains show no great change.

M.J. Jin

Papers

Annealing Of Cermic/Metal Graded Materials Fabricated By SHS/QP Method