Selective Laser Melting (SLM) is a particular rapid prototyping, 3D printing, or Additive Manufacturing (AM) technique designed to use high power-density laser to melt and fuse metallic powders. A component is built by selectively melting and fusing powders within and between layers. The SLM technique is also commonly known as direct selective laser sintering, LaserCusing, and direct metal laser sintering, and this technique has been proven to produce near net-shape parts up to 99.9% relative density. This enables the process to build near full density functional parts and has viable economic benefits. Recent developments of fibre optics and high-power laser have also enabled SLM to process different metallic materials, such as copper, aluminium, and tungsten. Similarly, this has also opened up research opportunities in SLM of ceramic and composite materials. The review presents the SLM process and some of the common physical phenomena associated with this AM technology. It then focuses on the following a...

/pdf/review-of-selective-laser-melting-materials-and-applications-2gpgz4zp60.pdf

Review of selective laser melting : materials and applications

On the mechanical behaviour of titanium alloy TiAl6V4 manufactured by selective laser melting: Fatigue resistance and crack growth performance

Al-12Si specimens are produced by selective laser melting (SLM) from gas atomized powders. An extremely fine cellular structure is observed with residual free Si along the cellular boundaries. Room temperature tensile tests reveal a remarkable mechanical behavior: the samples show yield and tensile strengths of about 260. MPa and 380. MPa, respectively, along with fracture strain of ~3%. The effect of annealing on microstructure and related tensile properties is examined and the results demonstrate that the mechanical behavior of the Al-12Si SLM samples can be tuned within a wide range of strength and ductility through proper annealing treatment.

Microstructure and mechanical properties of Al-12Si produced by selective laser melting: Effect of heat treatment

Triply periodic minimal surface (TPMS) structures have already been shown to be a versatile source of biomorphic scaffold designs. Therefore, in this work, Ti–6Al–4V Gyroid and Diamond TPMS lattices having an interconnected high porosity of 80–95% and pore sizes in the range of 560–1600 μm and 480–1450 μm respectively were manufactured by selective laser melting (SLM) for bone implants. The manufacturability, microstructure and mechanical properties of the Ti–6Al–4V TPMS lattices were evaluated. Comparison between 3D micro-CT reconstructed models and original CAD models of the Ti–6Al–4V TPMS lattices shows excellent reproduction of the designs. The as-built Ti–6Al–4V struts exhibit the microstructure of columnar grains filled with very fine and orthogonally oriented α′ martensitic laths with the width of 100–300 nm and have the microhardness of 4.01±0.34 GPa. After heat treatment at 680 °C for 4 h, the α′ martensite was converted to a mixture of α and β, in which the α phase being the dominant fraction is present as fine laths with the width of 500–800 nm and separated by a small amount of narrow, interphase regions of dark β phase. Also, the microhardness is decreased to 3.71±0.35 GPa due to the coarsening of the microstructure. The 80–95% porosity TPMS lattices exhibit a comparable porosity with trabecular bone, and the modulus is in the range of 0.12–1.25 GPa and thus can be adjusted to the modulus of trabecular bone. At the same range of porosity of 5–10%, the moduli of cortical bone and of the Ti–6Al–4V TPMS lattices are in a similar range. Therefore, the modulus and porosity of Ti–6Al–4V TPMS lattices can be tailored to the levels of human bones and thus reduce or avoid “stress shielding” and increase longevity of implants. Due to the biomorphic designs, and high interconnected porosity and stiffness comparable to human bones, SLM-made Ti–6Al–4V TPMS lattices can be a promising material for load bearing bone implants.

Ti–6Al–4V triply periodic minimal surface structures for bone implants fabricated via selective laser melting

Finite element modelling of the compressive response of lattice structures manufactured using the selective laser melting technique

Cellular materials are promising candidates for load adapted light-weight structures Direct manufacturing (DM) tools are effective methods to produce non-stochastic structures Many DM studies currently focus on optimization of the geometric nature of the structures obtained The literature available so far reports on the mechanical properties but local deformation mechanisms are not taken into account In order to fill this gap, the current study addresses the deformation behavior of a lattice structure produced by selective laser melting (SLM) on the local scale by means of a comprehensive experimental in situ approach, including electron backscatter diffraction, scanning electron microscopy and digital image correlation SLM-processed as well as heat treated lattice structures made from TiAl6V4 alloy were employed for mechanical testing It is demonstrated that the current approach provides means to understand the microstructure-mechanical property–local deformation relationship to allow for optimization of load adapted lattice structures

M. Thoene

Papers

In situ characterization of the deformation and failure behavior of non-stochastic porous structures processed by selective laser melting