This article reports on the International Nanofluid Property Benchmark Exercise, or INPBE, in which the thermal conductivity of identical samples of colloidally stable dispersions of nanoparticles or “nanofluids,” was measured by over 30 organizations worldwide, using a variety of experimental approaches, including the transient hot wire method, steady-state methods, and optical methods. The nanofluids tested in the exercise were comprised of aqueous and nonaqueous basefluids, metal and metal oxide particles, near-spherical and elongated particles, at low and high particle concentrations. The data analysis reveals that the data from most organizations lie within a relatively narrow band (±10% or less) about the sample average with only few outliers. The thermal conductivity of the nanofluids was found to increase with particle concentration and aspect ratio, as expected from classical theory. There are (small) systematic differences in the absolute values of the nanofluid thermal conductivity among the various experimental approaches; however, such differences tend to disappear when the data are normalized to the measured thermal conductivity of the basefluid. The effective medium theory developed for dispersed particles by Maxwell in 1881 and recently generalized by Nan et al. [J. Appl. Phys. 81, 6692 (1997)], was found to be in good agreement with the experimental data, suggesting that no anomalous enhancement of thermal conductivity was achieved in the nanofluids tested in this exercise.

A Benchmark Study on the Thermal Conductivity of Nanofluids

A review of recent advances in thermophysical properties at the nanoscale: From solid state to colloids

A review of thermal conductivity of various nanofluids

Stability of nanofluid: A review

A comprehensive review on graphene nanofluids: Recent research, development and applications

Stable and well dispersed functionalized graphene–ethylene glycol (EG) + distilled water nanofluids having graphene nano-sheets (GnS) volume concentration between 0.041 and 0.395 vol. % are prepared without any surfactant. Graphene nano-sheets are prepared from high purity graphite powder by Hummers method followed by exfoliation and reduction by hydrogen gas. Thus, obtained hydrogen exfoliated graphene (HEG) is then functionalized using acid. The graphene nano-sheets are characterized using XRD, TEM, Raman spectroscopy, and FTIR spectroscopy. Thermal conductivity and viscosity measurements are performed both as a function of graphene loading and temperature between 10 and 70 °C. Thermal conductivity enhancement of ∼15% for a loading of 0.395 vol. % f-HEG is observed at room temperature. The measured nanofluid's thermal conductivity is explained well in terms of the expression derived by Nan et al. (J. Appl. Phys. 81, 6692 (1997)), which considers matrix-additive interface contact resistance of mis-oriented ellipsoidal particles. The viscosity of the prepared f-HEG nanofluids and the base fluid (EG + distilled water) displays non-Newtonian behaviour with the appearance of shear thinning and nearly 100% enhancement compared to the base fluid (EG + DI water) with f-HEG loading of 0.395 vol. %. Known theoretical models for nanofluid's viscosity fail to explain the observed f-HEG volume concentration dependence of the nanofluid's viscosity. Temperature dependence of the studied nanofluid between 10 and 70 °C is explained well by the correlations proposed earlier for nanofluids with spherical nanoparticles. Electrical conductivity of the f-HEG nanofluids shows significant enhancement of ∼8620% for 0.395 vol. % loading of f-HEG in a base fluid of 70:30 mixture of EG and distilled water.

Madhusree Kole

Papers

Investigation of thermal conductivity, viscosity, and electrical conductivity of graphene based nanofluids