The influence of an electric current on the following solid state transformations in metals are considered: (1) intermetallic compound formation and growth in diffusion couples, (2) precipitation, (3) crystallization of amorphous alloys and (4) recrystallization and grain growth of cold worked metals. The formation and growth of intermetallic compounds were in qualitative accord with electromigration theory. Regarding precipitation, an electric current can either enhance or retard the precipitation rate, depending on the alloy, the current density and its frequency. Important factors appear to be the effect of current on the quenched-in vacancies and the presence of an internal stress. Both a continuous d.c. current and high current density electropulsing enhanced the crystallization rate of amorphous alloys. The effects are greater than can be explained by simple electromigration theory and suggest the cooperative motion of a larger number of atoms. Electropulsing enhanced the recrystallization rate of cold worked metals, but retarded subsequent grain growth. Enhancement of the recrystallization rate resulted mainly from an increase in the pre-exponential factor of the Arrhenius rate equation, which is considered to refer to the nucleation rate. Retardation of subsequent grain growth resulted from a lower residual dislocation density within the newly-formed grains.

Effects of electric current on solid state phase transformations in metals

Processing peculiarities and functions of alloying elements, such as Si and Mn, were studied for improving formability of steel sheets with mixed microstructures. Annealing a sheet steel with 0.2 pct C in the intercritical range produced very fine particles of retained austenite which were moderately stabilized due to C enrichment by subsequent holding in the bainite transformation range. Its strength-ductility balance is greatly superior to that of other dual-phase steels due to transformation-induced plasticity (TRIP). The holding time in the bainite transformation range varies with temperature, depending on the activation energy of C diffusion in austenite, and shifts to longer times with an increase of Si or Mn additions. The optimum cooling rate from the intercritical region is reduced with an increase of Mn content but is not influenced by Si content. Additional Mn makes the retained austenite content larger, although uniform elongation remains the same. In this case, the product of tensile strength and total elongation is increased due to an increase in the tensile strength. Contrary to Mn, Si does not affect retained austenite content but improves the uniform elongation by increasing its stability.

Mechanical Properties and Retained Austenite in Intercritically Heat-Treated Bainite-Transformed Steel and Their Variation with Si and Mn Additions

On the thermodynamics and kinetics of electropulsing induced dissolution of β-Mg17Al12 phase in an aged Mg–9Al–1Zn alloy

The effect of phosphorus and silicon on the formation of retained austenite has been investigated in a low-carbon steel cold rolled, intercritically annealed, and isothermally held in a temperature range of bainitic transformation followed by air cooling. The steel sheet containing phosphorus after final heat-treatment consisted of ferrite, retained austenite, and bainite or martensite. Phosphorus, especially in the presence of silicon, in steel was useful to assist the formation of retained austenite. Mechanical properties, such as tensile strength, uniform elongation, and the combination of tensile strength/ductility, were improved when phosphorus was increased up to 0.07 pct in 0.5 pct Si steel. This could be attributed to the strain-induced transformation of retained austenite during tensile deformation. Furthermore, two types of retained austenite were observed in P-containing steel. One is larger than about 1 μm in size and usually exists adjacent to bainite; the other one is of submicron size and usually exists in a ferrite matrix. High phosphorus content promotes the formation of stable (small size) austenites which are considered to be stabilized mainly by their small size effect and have a different formation mechanism from the coarser retained austenite in the lower P steels. The retained austenites of submicron size showed mechanical stability even after 10 pct deformation, suggesting that these small austenites have little effect on ductility. The 0.07 pct P-0.5 pct Si-1.5 pct Mn-0.12 pct C steel showed a high strength of 730 MPa and a total elongation of 36 pct.

Nasser Karam

Papers

Effect of electric current pulses on the recrystallization of copper

Effect of prior cold work on the influence of electric current pulses on the recrystallization of copper

Effect of electric current pulses on the recrystallization kinetics of copper