Large-grain high-temperature superconductors of the form RE-Ba-Cu-O (where RE is a rare-earth element) can trap magnetic fields of several tesla at low temperatures, and so can be used for permanent magnet applications. The magnitude of the trapped field is proportional to the critical current density and the volume of the superconductor. Various potential engineering applications for such magnets have emerged, and some have already been commercialized. However, the range of applications is limited by poor mechanical stability and low thermal conductivity of the bulk superconductors; RE-Ba-Cu-O magnets have been found to fracture during high-field activation, owing to magnetic pressure. Here we present a post-fabrication treatment that improves the mechanical properties as well as thermal conductivity of a bulk Y-Ba-Cu-O magnet, thereby increasing its field-trapping capacity. First, resin impregnation and wrapping the materials in carbon fibre improves the mechanical properties. Second, a small hole drilled into the centre of the magnet allows impregnation of Bi-Pb-Sn-Cd alloy into the superconductor and inclusion of an aluminium wire support, which results in a significant enhancement of thermal stability and internal mechanical strength. As a result, 17.24 T could be trapped, without fracturing, in a bulk Y-Ba-Cu-O sample of 2.65 cm diameter at 29 K.

High-temperature superconductor bulk magnets that can trap magnetic fields of over 17 tesla at 29 K

A reduced oxygen atmosphere during melt processing turned out to be critical for the fabrication of NdBa2Cu3Oy (Nd123) superconductors possessing high superconducting transition temperature (Tc) with a sharp transition and large critical current density (Jc) at 77 K. In a dc magnetization measurement, Nd123 superconductors melt processed in flowing a mixture gas of 1% O2 in Ar exhibited the Tc of about 95 K and the transition width of 1.5 K with the applied field of 10 Oe. A four‐probe measurement showed the zero resistive transition Tc (R=0) of about 95 K. An anomalous peak effect in the magnetization hysteresis (M‐H) loops was commonly observed and lead to large magnetic Jc of 2×104 A/cm2 at 77 K and 2 T for the applied field H parallel to the c axis of a sample (H∥c). This achievement is attributable to a preferential formation of high Tc phase (x<0.1) among the Nd1+xBa2−xCu3Oy solid solutions in a reduced oxygen atmosphere.

Melt processing for obtaining NdBa2Cu3Oy superconductors with high Tc and large Jc

A magnetoresistive element according to an embodiment includes: a first ferromagnetic layer having an axis of easy magnetization in a direction perpendicular to a film plane; a second ferromagnetic layer having an axis of easy magnetization in a direction perpendicular to a film plane; a nonmagnetic layer placed between the first ferromagnetic layer and the second ferromagnetic layer; a first interfacial magnetic layer placed between the first ferromagnetic layer and the nonmagnetic layer; and a second interfacial magnetic layer placed between the second ferromagnetic layer and the nonmagnetic layer The first interfacial magnetic layer includes a first interfacial magnetic film, a second interfacial magnetic film placed between the first interfacial magnetic film and the nonmagnetic layer and having a different composition from that of the first interfacial magnetic film, and a first nonmagnetic film placed between the first interfacial magnetic film and the second interfacial magnetic film

Magnetoresistive element and magnetic memory

Unlike Y123 which forms only a stoichiometric compound, the light rare earth elements (LREs: La, Nd, Sm, Eu, Gd) form a solid solution . The presence of such solid solution caused a depression in the superconducting transition temperatures , particularly for La123, Nd123 and Sm123 when they are melt processed in air. Recently, we have found that the of these LRE123 superconductors can greatly be enhanced when they are melt processed in a reduced oxygen atmosphere. Furthermore, values of these superconductors were larger than that of a good quality Y123 superconductor in high magnetic fields at 77 K. In this article, on the basis of our study over the last several years, the melt processes for LRE - Ba - Cu - O are described, the microstructural and superconducting properties of the superconductors are reviewed and the flux pinning mechanism is also discussed.

https://iopscience.iop.org/article/10.1088/0953-2048/9/12/001/pdf

Melt-processed light rare earth element - Ba - Cu - O

/pdf/topical-review-superconducting-bearings-3qs5e8w9gs.pdf

TOPICAL REVIEW: Superconducting bearings

REBa2Cu3Oy superconductors with rare earth (RE) ions with large radii (RE: La, Nd, Sm) exhibit relatively low T c due to the presence of RE-Ba solid solution. We have found that this solid solution can be suppressed if these superconductors are melt processed in a reduced oxygen atmosphere. We have also found that critical current densities of these superconductors are higher than those of melt processed YBa2Cu3Oy with fine Y2BaCuO5 inclusions in a high field region. The irreversibility line was also shifted toward the higher H-T region. We believe that flux pinning in these superconductors is ascribable to a finely distributed RE(Ba1-x , REx )2Cu3Oy phase in a good superconductive matrix.

https://iopscience.iop.org/article/10.1143/JJAP.33.L715/pdf

Flux pinning in melt-grown NdBa2Cu3Oy and SmBa2Cu3Oy superconductors

Analysis of pinning in superconductors

Comparative study of critical current densities and flux pinning among a flux-grown NdBa2Cu3Oy single crystal, melt-textured Nd-Ba-Cu-O, and Y-Ba-Cu-O bulks

Takamitsu Higuchi

Papers

Melt processing for obtaining NdBa2Cu3Oy superconductors with high Tc and large Jc

Melt-processed light rare earth element - Ba - Cu - O

Flux pinning in melt-grown NdBa2Cu3Oy and SmBa2Cu3Oy superconductors

Analysis of pinning in superconductors

Comparative study of critical current densities and flux pinning among a flux-grown NdBa2Cu3Oy single crystal, melt-textured Nd-Ba-Cu-O, and Y-Ba-Cu-O bulks