2.3. Evaluation of Photocatalytic Water Splitting 6507 2.3.1. Photocatalytic Activity 6507 2.3.2. Photocatalytic Stability 6507 3. UV-Active Photocatalysts for Water Splitting 6507 3.1. d0 Metal Oxide Photocatalyts 6507 3.1.1. Ti-, Zr-Based Oxides 6507 3.1.2. Nb-, Ta-Based Oxides 6514 3.1.3. W-, Mo-Based Oxides 6517 3.1.4. Other d0 Metal Oxides 6518 3.2. d10 Metal Oxide Photocatalyts 6518 3.3. f0 Metal Oxide Photocatalysts 6518 3.4. Nonoxide Photocatalysts 6518 4. Approaches to Modifying the Electronic Band Structure for Visible-Light Harvesting 6519

Semiconductor-based Photocatalytic Hydrogen Generation

Nano-sized TiO 2 photocatalytic water-splitting technology has great potential for low-cost, environmentally friendly solar-hydrogen production to support the future hydrogen economy. Presently, the solar-to-hydrogen energy conversion efficiency is too low for the technology to be economically sound. The main barriers are the rapid recombination of photo-generated electron/hole pairs as well as backward reaction and the poor activation of TiO 2 by visible light. In response to these deficiencies, many investigators have been conducting research with an emphasis on effective remediation methods. Some investigators studied the effects of addition of sacrificial reagents and carbonate salts to prohibit rapid recombination of electron/hole pairs and backward reactions. Other research focused on the enhancement of photocatalysis by modification of TiO 2 by means of metal loading, metal ion doping, dye sensitization, composite semiconductor, anion doping and metal ion-implantation. This paper aims to review the up-to-date development of the above-mentioned technologies applied to TiO 2 photocatalytic hydrogen production. Based on the studies reported in the literature, metal ion-implantation and dye sensitization are very effective methods to extend the activating spectrum to the visible range. Therefore, they play an important role in the development of efficient photocatalytic hydrogen production.

A review and recent developments in photocatalytic water-splitting using TiO2 for hydrogen production

Generations Yi Ma,† Xiuli Wang,† Yushuai Jia,† Xiaobo Chen,‡ Hongxian Han,*,† and Can Li*,† †State Key Laboratory of Catalysis, Dalian Institute of Chemical Physics, Chinese Academy of Sciences and Dalian National Laboratory for Clean Energy, 457 Zhongshan Road, Dalian 116023, China ‡Department of Chemistry, College of Arts and Sciences, University of Missouri-Kansas City, 5100 Rockhill Road, Kansas City, Missouri 64110, United States

Titanium dioxide-based nanomaterials for photocatalytic fuel generations.

A surface science perspective on TiO2 photocatalysis

Nitrogen-doped TiO2 (N−TiO2) nanocatalyst with spherical shape and homogeneous size has been synthesized through a chemical method using TiCl3 as precursor. The light absorption onset shifts from 380 nm on pure TiO2 to the visible region at 550 nm with N−TiO2. A clear decrease in the band gap and the nitrogen 2p states on the top of the valence band on N−TiO2 (compared to TiO2) is deduced from the optical absorption spectroscopy results. The chemical nature of N has been evolved as N−Ti−O in the anatase TiO2 lattice as identified by X-ray photoelectron spectroscopy (XPS). Photocatalytic decomposition of methylene blue has been carried out both in the UV and in the visible region and N−TiO2 shows higher activity than the Degussa P25 TiO2 photocatalyst in the visible region.

Synthesis, Characterization, Electronic Structure, and Photocatalytic Activity of Nitrogen-Doped TiO2 Nanocatalyst

Nitrogen-doped titanium dioxide (TiO 2 ) powders were prepared by the heating of titanium hydroxide with urea The samples had a relatively larger specific surface area of 92 ± 2 m 2  g −1 and showed visible-light photocatalytic activity of about 550 nm

Y. Murakami

Papers

Visible-light active N-doped TiO2 prepared by heating of titanium hydroxide and urea