This paper presents a review of the principal developments in functionally graded materials (FGMs) with an emphasis on the recent work published since 2000. Diverse areas relevant to various aspects of theory and applications of FGM are reflected in this paper. They include homogenization of particulate FGM, heat transfer issues, stress, stability and dynamic analyses, testing, manufacturing and design, applications, and fracture. The critical areas where further research is needed for a successful implementation of FGM in design are outlined in the conclusions. DOI: 10.1115/1.2777164

https://web.mst.edu/~vbirman/papers/Modeling%20and%20Analysis%20of%20FGM_Review_2007.pdf

Modeling and Analysis of Functionally Graded Materials and Structures

http://user.engineering.uiowa.edu/~rahman/efm_fgm.pdf

Mesh-free analysis of cracks in isotropic functionally graded materials

Mixed-mode fracture of orthotropic functionally graded materials using finite elements and the modified crack closure method

The interaction integral for fracture of orthotropic functionally graded materials: Evaluation of stress intensity factors

The weight function method is described to analyze the crack growth behavior in functionally graded materials and in particular materials with a rising crack growth resistance curve. Further, failure of graded thermal barrier coatings (TBCs) under cyclic surface heating by laser irradiation is modeled on the basis of fracture mechanics. The damage of both graded and non-graded TBCs is found to develop in several distinct stages: vertical cracking → delamination → blistering → spalling . This sequence can be understood as an effect of progressive shrinkage due to sintering and high-temperature creep during thermal cycling, which increases the energy-release rate for vertical cracks which subsequently turn into delamination cracks. The results of finite element modeling, taking into account the TBC damage mechanisms, are compatible with experimental data. An increase of interface fracture toughness due to grading and a decrease due to ageing have been measured in a four-point bending test modified by a stiffening layer. Correlation with the damage observed in cyclic heating is discussed. It is explained in which way grading is able to reduce the damage.

/pdf/cracks-in-functionally-graded-materials-4amqa1gc61.pdf

Y.Y. Yang

Papers

Cracks in functionally graded materials

The regular stress term in bonded dissimilar materials after a change in temperature

Applicability of the extended Petroski–Achenbach weight function procedure to graded materials