Surface modification of titanium and titanium alloys: Technologies, developments, and future interests

Recent advances in biodegradation controls over Mg alloys for bone fracture management: A review

Electrochemical surface engineering of titanium-based alloys for biomedical application

Periprosthetic infection is considered the main cause of implant failure, which is expected to be solved by fabricating an antibacterial coating on the surface of the implant. Nevertheless, systemic antibiotic treatment still represents the mainstream method for preventing infection, and few antibacterial coatings are applied clinically. This is because the externally introduced traditional antibacterial coatings suffer from the risk of invalidation and tissue toxicity induced by the consumption of antibacterial agents, degradation, and shedding. In this work, we proposed a rapid photo-sonotherapy by creating an oxygen deficiency on a titanium (Ti) implant through sulfur (S)-doping (Ti-S-TiO2-x), which endowed the implants with great sonodynamic and photothermal ability. Without introducing an external antibacterial coating, it reached a high antibacterial efficiency of 99.995% against Staphylococcus aureus under 15 min near-infrared light and ultrasound treatments. Furthermore, bone infection was successfully treated after combination treatments, and improved osseointegration was observed. Importantly, the S-doped Ti implant immersed in water for 6 months showed an unchanged structure and properties, suggesting that the Ti implant with intrinsic modification showed stable antibacterial performance under exogenous stimuli with a high antibacterial performance in vivo. This photo-sonotherapy based on sulfur doping is also promising for cancer therapy with biosafety.

Rapid Photo-Sonotherapy for Clinical Treatment of Bacterial Infected Bone Implants by Creating Oxygen Deficiency Using Sulfur Doping

The bioactive and anti-bacterial Cu-based bioceramic TiO2 coatings have been fabricated on cp-Ti (Grade 2) by two-steps. These two-steps combine micro-arc oxidation (MAO) and physical vapor deposition–thermal evaporation (PVD-TE) techniques for dental implant applications. As a first step, all surfaces of cp-Ti substrate were coated by MAO technique in an alkaline electrolyte, consisting of Na3PO4 and KOH in de-ionized water. Then, as a second step, a copper (Cu) nano-layer with 5 nm thickness was deposited on the MAO by PVD-TE technique. Phase structure, morphology, elemental amounts, thickness, roughness and wettability of the MAO and Cu-based MAO coating surfaces were characterized by XRD (powder- and TF-XRD), SEM, EDS, eddy current device, surface profilometer and contact angle goniometer, respectively. The powder- and TF-XRD spectral analyses showed that Ti, TiO2, anatase-TiO2 and rutile-TiO2 existed on the MAO and Cu-based MAO coatings’ surfaces. All coatings’ surfaces were porous and rough, owing to the presence of micro sparks through MAO. Furthermore, the surface morphology of Cu-based MAO was not changed. Also, the Cu-based MAO coating has more hydrophilic properties than the MAO coating. In vitro bioactivity and in vitro antibacterial properties of the coatings have been investigated by immersion in simulated body fluid (SBF) at 36.5 °C for 28 days and bacterial adhesion for gram-positive (S. aureus) and gram-negative (E. coli) bacteria, respectively. The apatite layer was formed on the MAO and Cu-based MAO surfaces at post-immersion in SBF and therefore, the bioactivity of Cu-based MAO surface was increased to the MAO surface. Also, for S. aureus and E. coli, the antibacterial properties of Cu-based MAO coatings were significantly improved compared to one of the uncoated MAO surfaces. These results suggested that Cu-based MAO coatings on cp-Ti could be a promising candidate for biomedical dental implant applications.

/pdf/characterization-bioactivity-and-antibacterial-properties-of-1z15mk8ren.pdf

Yi Wang

Papers

Review of the biocompatibility of micro-arc oxidation coated titanium alloys