If a composite under impact failure starting wih compression or tension?
Best insight from top research papers
Composite failure under impact can start with either compression or tension loading . The failure mechanisms involved in composite failure under impact include matrix failure, delamination, and fiber failure . The use of Non-Destructive Techniques (NDTs) such as ultrasonic C-scan and X-ray radiography can be helpful in identifying damage inside the laminate, especially Barely Visible Impact Damage (BVID) . Fractographic techniques can also be used to understand the progression of damage in the laminate . The presence of initial delamination defects in carbon fiber-reinforced polymer (CFRP) composite laminates can affect the evolution of mechanical properties and impact response . Low-velocity impact on composite laminates can result in multiple failure mechanisms such as matrix cracking, fiber breakage, and interface delaminations . The failure mechanism of 3D woven composites under compression loading after low-velocity impact is influenced by the weft and warp orientations . The shear stress component resulting from longitudinal tension and fiber misalignment can cause matrix failure before fiber break in unidirectional composites .
Answers from top 5 papers
More filters
| Papers (5) | Insight |
|---|---|
1 Citations | The provided paper does not mention anything about the impact failure of a composite starting with compression or tension. |
| The provided paper does not explicitly mention whether the failure of the composite under impact starts with compression or tension. | |
07 Nov 2018 1 Citations | The paper does not explicitly mention whether the composite laminate under impact failure starts with compression or tension. |
| The paper does not explicitly mention whether a composite under impact failure starts with compression or tension. | |
3 Citations | The provided paper does not directly mention whether the failure of the composite under impact starts with compression or tension. |
Related Questions
What is composite reliability in analysis?5 answersComposite reliability in analysis refers to the assessment of the probability that a system, such as a power system or a composite material, will consistently perform its intended function under various uncertainties and variations. This involves quantifying the likelihood of successful operation while considering factors like material properties, manufacturing processes, and external influences. For instance, in the context of composite materials, reliability analysis accounts for uncertainties in resin content, curing, and defects, providing a probabilistic distribution of product properties. In power systems, the increasing deployment of renewable energy sources adds complexity, necessitating new operational approaches to enhance reliability. By utilizing probabilistic modeling techniques like Monte Carlo simulations and the First-Order Reliability Method, composite reliability analysis aids in decision-making for both production and performance optimization.
How dent depth and contact force affect the impact resistance of composite cylinder?5 answersThe impact resistance of composite cylinders is influenced by dent depth and contact force. For composite/metal hybrid structures like those in CNG cylinders, changes in structure affect impact energy absorption rate and load-bearing capacity. In thin-walled carbon fiber reinforced epoxy composite cylinders, the stacking sequence plays a crucial role in impact resistance, with certain sequences showing higher resistance. Analytical scaling factors can aid in assessing impact resistance of laminated plates and shells with orthotropic properties. Dynamic responses of laminated composite cylindrical shells under impact are analyzed using nonlinear finite element methods, considering factors like contact force, deflections, and strains. Dent depth and contact force correlations provide valuable insights for designing composite structures with enhanced impact resistance in various applications.
Investigating damage as impact resistance paramaters on composite cylinder ?5 answersDamage investigation in composite cylinders for impact resistance parameters involves various approaches. Studies have utilized gas gun tests to evaluate impact performance, with numerical simulations matching test results on damage morphology and impact acceleration-time curves. The impact resistance of fiber-reinforced polymer composites has been a focus, with computational models analyzing damage progression and energy evolution to understand failure processes. Hybrid composite/metal structures in CNG cylinders have shown altered impact damage characteristics, affecting parameters like impact energy absorption rate and delamination extension resistance. Additionally, optical-fiber-embedded cylinders have been subjected to impact events, measuring residual strain to assess damage maps and energy proportionality. These diverse studies provide insights into the complex nature of damage assessment for enhancing the impact resistance of composite cylinders.
Is Higher contact force, higher the impact resistances of composite?5 answersHigher contact force does not necessarily guarantee higher impact resistance of composites. Impact resistance is influenced by various factors such as material composition, reinforcement structures, and matrix properties. For instance, the study on hybrid fabric-reinforced polymer composites found that the number of Kevlar layers significantly impacted impact resistance, with neat Kevlar/epoxy composites exhibiting the best performance. Additionally, the use of novel steel fibers in composites showed high potential toughness due to their unique properties. Therefore, while contact force may play a role, the overall impact resistance of composites is a complex interplay of multiple factors beyond just the force applied.
What are the failure criteria for polymer composite materials?5 answersFailure criteria for polymer composite materials include stress-based failure criteria, stress gradient-based failure criteria, and unified failure criteria. The stress-based failure criteria determine potential failure locations based on stress conditions, while the stress gradient-based failure criteria consider the cubic power of the effective stress divided by its stress gradient. Both conditions must be satisfied for failure to occur. Unified failure criteria combine stress and strain conditions with stress and strain gradient conditions, and they can be applied to any shape of defect. These criteria provide not only failure locations but also directions of failure propagation. Other widely used failure criteria for polymer composites include the Maximum Stress, Tsai-Wu, Hoffman, Tsai-Hill, Hashin, and Puck criteria, which have been applied in numerical simulations and validated through experimental tests. Micromechanical analysis and virtual experimental testing methodologies have also been used to assess failure criteria and develop failure envelopes for carbon fiber-reinforced polymer composites.
How is the load bearing capacity for in-plane loads in composite materials linked to intralaminar/translaminar damage?4 answersThe load bearing capacity for in-plane loads in composite materials is linked to intralaminar and translaminar damage. Intralaminar damage, such as debonding between fibers and matrix, can lead to the onset of damage in the weakest lamina, while translaminar damage refers to the progression of damage through the matrix or along the interfaces between fibers and matrix, resulting in transverse cracks in the laminate. The presence of intralaminar damage promotes fiber bridging in the transverse direction, which significantly influences the out-of-plane properties of the composite. The extent of delamination, a form of translaminar damage, is studied to understand the impact resistance of composite laminates under low velocity impact loading. The development of predictive numerical methods, such as the phase field approach of fracture, can accurately represent the progressive failure of composite laminates and provide insights into intralaminar and translaminar fracture mechanisms.