Showing papers by "Bizhou Lin published in 2012"
••
TL;DR: The O-doping in the g-C(3)N(4) lattice could induce intrinsic electronic and band structure modulation, resulting in its absorbance edge up to 498 nm and enhanced visible-light photoactivity, consequently.
887 citations
••
TL;DR: Anatase TiO 2 -pillared HTaWO 6 was prepared by assembling tantalotungstate nanosheets with anataseTiO 2 nanoparticles via an exfoliation-restacking route as discussed by the authors.
43 citations
••
TL;DR: In this paper, a mesoporous anatase TiO2-pillared hexaniobate has been successfully prepared by an exfoliation-restacking route, and the resulting nanocomposite was characterized by powder X-ray diffraction, Xray photoelectron spectroscopy, scanning electron microscope, thermogravimetric analysis, UV-Vis spectroscopic and N2 adsorption-desorption measurements.
21 citations
••
TL;DR: In this paper, a mesoporous layered tantalotungstate nanosheets with manganese ions via an exfoliation-restacking route is presented. But the mesopores are derived from the stacking of the intercalated crystallites.
17 citations
••
TL;DR: In this paper, a photoelectrocatalytic degradation of Rhodamine B with the exfoliated TiNbO 5 nanosheets was investigated, which revealed that both the oxygen anionic radicals and the dye cationic radical are essential for the mineralization of the dye under visible light driven photocatalytic conditions.
16 citations
••
TL;DR: The pillared nanaocomposite exhibited enhanced photocatalytic activity in the photodegradation of Rhodamine B under UV light irradiation, and is attributed to the electronic coupling between the host and the guest components, as well as its high surface area and mesoporosity.
13 citations
••
TL;DR: In this article, a layered compound HLa 0.90 Dy 0.05 Nb 2 O 7 nanosheets were exfoliated by a layer-by-layer deposition technology, which were subsequently heat-treated at 450°C and exposed under ultraviolet light to obtain the polymer-free nanosheet films, respectively.
5 citations