Crack Propagation under Fatigue-Creep Conditions and Fractography
TLDR
In this paper, the crack propagation of a 304 stainless steel under repeated load at elevated temperatures was examined using specimens of different size to clarify the successful correlating parameter, and the results were discussed in the light of electron fractography.Abstract:
The crack propagation of a 304 stainless steel under repeated load at elevated temperatures was critically examined using specimens of different size to clarify the successful correlating parameter, and the results were discussed in the light of electron fractography. The crack propagation rate at 250 and 500°C where creep is not significant in this material was correlated with the stress intensityread more
Citations
More filters
Journal ArticleDOI
Application of fracture mechanics to the surface crack propagation in stainless steel at elevated temperatures
TL;DR: In this paper, the propagation of small surface cracks in SUS 304 stainless steel is examined at elevated temperatures in the presence of cyclic deformation and elastic-plastic fracture mechanics parameters.