Au-Ti-SBA-15 catalysts have been synthesized using different preparation routes. Ti-SBA-15 supports with Si/Ti ratio ranging from 10 to 80 have been prepared by grafting and direct synthesis. X-ray fluorescence (XRF), X-ray diffraction (XRD), diffuse reflectance UV-visible spectroscopy (DRS), transmission electron microscopy (TEM) and nitrogen sorption were applied for the characterization of the prepared catalysts. The catalytic activities of the Au/Ti-SBA-15 materials have been investigated in the direct epoxidation of propene by using a mixture of H2 and O2 and its performance was compared with an Au/TiO2 catalyst. The activity results were then interpreted with reference to the characterization.

Propene oxide is a very important intermediate for the synthesis of commercial products, including adhesives, paints, and cosmetics. The gas-phase epoxidation of propene over Au/Ti-based catalysts is an intriguing scientific topic, not only because of the industrial importance of the production of propene oxide, but also because this reaction offers fundamental insights into the working principles of Au-based catalysis. The current methods used for propene oxide synthesis combine several reaction steps and have economic or environmental problems. Au/Ti-based catalysts are able to produce propene oxide with high selectivity out of propene, hydrogen and oxygen in a simple process since a single reactor is needed. However, a fundamental understanding of the reaction mechanism is necessary for developing more efficient Au/Ti-based propene epoxidation catalysts. The aim of this PhD thesis was to shed further insight into the mechanism of Au/Ti-based catalysts for the epoxidation of propene with O2 and H2. The first effort of the research has focused on the synthesis of well-defined Au/Ti-SBA-15 catalysts. Different methods have been used for the synthesis of the Ti-SBA-15 supports. Au/Ti-SBA-15 prepared by grafting Ti in the SBA-15 structure contains a higher absolute amount of tetrahedral Ti than the ones prepared by a hydrothermal method of Ti-SBA-15 support. The catalytic activity of Au/Ti-SBA-15 catalysts was found to be dependent on the amount and dispersion of Ti as well on the Au particle size. Further more, the epoxidation activity of Au/Ti-SBA-15 catalysts was improved by performing a post-synthesis NH4NO3 treatment. Formation of a large number of surface hydroxyl groups together with ammonium species on the surface support have a beneficial effect on the homogeneous deposition of Au. The superior activity of treated Au/Ti-SBA-15 materials is related to the increased number of Au adsorption sites. Several spectroscopic techniques were used for characterization of the resulted catalysts and for understanding of the reaction mechanism. In-situ XAFS spectroscopy provided evidence on the adsorption of propene on Au nanoparticles. The results indicated that the adsorption of propene is a key step in the epoxidation mechanism over Au/Ti-based catalysts. Furthermore, steady state isotopic kinetic analysis performed on Au/TiO2 and Au/Ti-SBA-15 was used to investigate if the support oxygen is playing a role in the production of propene oxide. The results obtained from our studies were discussed together with the literature reports in order to understand the related propene epoxidation mechanism.

/pdf/new-mechanistic-insight-in-the-gold-based-propene-176bm9phm9.pdf

Synthesis and characterization of Au/Ti-SBA-15 catalysts for the vapour phase epoxidation of propylene

Citations

New mechanistic insight in the gold-based propene epoxidation

Related Papers (5)

Propene epoxidation over Au/Ti-SBA-15 catalysts

Hydrogenation of Tetralin Over Ir Catalysts Supported on Titania-Modified SBA-16

Characterization and catalytic performance of Co/SBA-15 supported gold catalysts for CO oxidation

Ultrasound-assisted synthesis and catalytic activity of mesostructured FeOx/SBA-15 and FeOx/Zr-SBA-15 catalysts for the oxidative desulfurization of model diesel

Synthesis and characterization of Mn3O4 and Mn2O3 nanocrystals on SBA-15: Novel combustion catalysts at low reaction temperatures