The immediate bonding effectiveness of contemporary adhesives is quite favorable, regardless of the approach used. In the long term, the bonding effectiveness of some adhesives drops dramatically, whereas the bond strengths of other adhesives are more stable. This review examines the fundamental processes that cause the adhesion of biomaterials to enamel and dentin to degrade with time. Non-carious class V clinical trials remain the ultimate test method for the assessment of bonding effectiveness, but in addition to being high-cost, they are time- and labor-consuming, and they provide little information on the true cause of clinical failure. Therefore, several laboratory protocols were developed to predict bond durability. This paper critically appraises methodologies that focus on chemical degradation patterns of hydrolysis and elution of interface components, as well as mechanically oriented test set-ups, such as fatigue and fracture toughness measurements. A correlation of in vitro and in vivo data revealed that, currently, the most validated method to assess adhesion durability involves aging of micro-specimens of biomaterials bonded to either enamel or dentin. After about 3 months, all classes of adhesives exhibited mechanical and morphological evidence of degradation that resembles in vivo aging effects. A comparison of contemporary adhesives revealed that the three-step etch-and-rinse adhesives remain the 'gold standard' in terms of durability. Any kind of simplification in the clinical application procedure results in loss of bonding effectiveness. Only the two-step self-etch adhesives approach the gold standard and do have some additional clinical benefits.

http://www.endoexperience.com/documents/DeMunketalDurabiltyofadhesionJDR.pdf

A Critical Review of the Durability of Adhesion to Tooth Tissue: Methods and Results

Bonding to tooth tissue can be achieved through an "etch&rinse," "self-etch" or "glass-ionomer" approach. In this paper, the basic bonding mechanism to enamel and dentin of these three approaches is demonstrated by means of ultramorphological and chemical characterization of tooth-biomaterial interfacial interactions. Furthermore, bond-strength testing and measurement of marginal-sealing effectiveness (the two most commonly employed methodologies to determine "bonding effectiveness" in the laboratory) are evaluated upon their value and relevance in predicting clinical performance. A new dynamic methodology to test biomaterial-tooth bonds in a fatigue mode is introduced with a recently developed micro-rotary fatigue-testing device. Eventually, today's adhesives will be critically weighted upon their performance in diverse laboratory studies and clinical trials. Special attention has been given to the benefits/drawbacks of an etch&rinse versus a self-etch approach and the long-term performance of these adhesives. Correlating data gathered in the laboratory with clinical results clearly showed that laboratory research CAN predict clinical effectiveness. Although there is a tendency to simplify bonding procedures, the data presented confirm that conventional three-step etch&rinse adhesives still perform most favorably and are most reliable in the long-term. Nevertheless, a self-etch approach may have the best future perspective. Clinically, when adhesives no longer require an "etch&rinse" step, the application time, and probably more importantly, the technique-sensitivity are substantially reduced. Especially "mild," two-step self-etch adhesives that bond through a combined micromechanical and chemical interaction with tooth tissue closely approach conventional three-step systems in bonding performance.

Buonocore memorial lecture, adhesion to enamel and dentin: current status and future challenges

Systematic review of the chemical composition of contemporary dental adhesives

Dental adhesion review: Aging and stability of the bonded interface

http://webdelprofesor.ula.ve/odontologia/robertramirez/PDF/1.pdf

State of the art of self-etch adhesives

Mild self-etch adhesives demineralize dentin only partially, leaving hydroxyapatite around collagen within a submicron hybrid layer. We hypothesized that this residual hydroxyapatite may serve as a receptor for chemical interaction with the functional monomer and, subsequently, contribute to adhesive performance in addition to micro-mechanical hybridization. We therefore chemically characterized the adhesive interaction of 3 functional monomers with synthetic hydroxyapatite, using x-ray photoelectron spectroscopy and atomic absorption spectrophotometry. We further characterized their interaction with dentin ultra-morphologically, using transmission electron microscopy. The monomer 10-methacryloxydecyl dihydrogen phosphate (10-MDP) readily adhered to hydroxyapatite. This bond appeared very stable, as confirmed by the low dissolution rate of its calcium salt in water. The bonding potential of 4-methacryloxyethyl trimellitic acid (4-MET) was substantially lower. The monomer 2-methacryloxyethyl phenyl hydrogen phosphate (phenyl-P) and its bond to hydroxyapatite did not appear to be hydrolytically stable. Besides self-etching dentin, specific functional monomers have additional chemical bonding efficacy that is expected to contribute to their adhesive potential to tooth tissue.

Comparative Study on Adhesive Performance of Functional Monomers

Functional monomers chemically interact with hydroxyapatite that remains within submicron hybrid layers produced by mild self-etch adhesives. The functional monomer 10-MDP interacts most intensively with hydroxyapatite, and its calcium salt appeared most hydrolytically stable, as compared with 4-MET and phenyl-P. We investigated the hypothesis that additional chemical interaction of self-etch adhesives improves bond stability. The micro-tensile bond strength (muTBS) of the 10-MDP-based adhesive did not decrease significantly after 100,000 cycles, but did after 50,000 and 30,000 cycles, respectively, for the 4-MET-based and the phenyl-P-based adhesives. Likewise, the interfacial ultrastructure was unchanged after 100,000 thermocycles for the 10-MDP-based adhesive, while that of both the 4-MET- and phenyl-P-based adhesives contained voids and less-defined collagen. The findings of this study support the concept that long-term durability of adhesive-dentin bonds depends on the chemical bonding potential of the functional monomer.

K. Nagakane

Papers

Comparative Study on Adhesive Performance of Functional Monomers

Hydrolytic Stability of Self-etch Adhesives Bonded to Dentin