The interest in nanoscale materials stems from the fact that new properties are acquired at this length scale and, equally important, that these properties * To whom correspondence should be addressed. Phone, 404-8940292; fax, 404-894-0294; e-mail, mostafa.el-sayed@ chemistry.gatech.edu. † Case Western Reserve UniversitysMillis 2258. ‡ Phone, 216-368-5918; fax, 216-368-3006; e-mail, burda@case.edu. § Georgia Institute of Technology. 1025 Chem. Rev. 2005, 105, 1025−1102

Chemistry and properties of nanocrystals of different shapes.

Monodisperse samples of silver nanocubes were synthesized in large quantities by reducing silver nitrate with ethylene glycol in the presence of poly(vinyl pyrrolidone) (PVP). These cubes were single crystals and were characterized by a slightly truncated shape bounded by {100}, {110}, and {111} facets. The presence of PVP and its molar ratio (in terms of repeating unit) relative to silver nitrate both played important roles in determining the geometric shape and size of the product. The silver cubes could serve as sacrificial templates to generate single-crystalline nanoboxes of gold: hollow polyhedra bounded by six {100} and eight {111} facets. Controlling the size, shape, and structure of metal nanoparticles is technologically important because of the strong correlation between these parameters and optical, electrical, and catalytic properties.

http://science.sciencemag.org/content/sci/298/5601/2176.full.pdf

Shape-Controlled Synthesis of Gold and Silver Nanoparticles

This review focuses on the synthesis, protection, functionalization, and application of magnetic nanoparticles, as well as the magnetic properties of nanostructured systems. Substantial progress in the size and shape control of magnetic nanoparticles has been made by developing methods such as co-precipitation, thermal decomposition and/or reduction, micelle synthesis, and hydrothermal synthesis. A major challenge still is protection against corrosion, and therefore suitable protection strategies will be emphasized, for example, surfactant/polymer coating, silica coating and carbon coating of magnetic nanoparticles or embedding them in a matrix/support. Properly protected magnetic nanoparticles can be used as building blocks for the fabrication of various functional systems, and their application in catalysis and biotechnology will be briefly reviewed. Finally, some future trends and perspectives in these research areas will be outlined.

Magnetic nanoparticles: Synthesis, protection, functionalization, and application

Nanocrystals are fundamental to modern science and technology. Mastery over the shape of a nanocrystal enables control of its properties and enhancement of its usefulness for a given application. Our aim is to present a comprehensive review of current research activities that center on the shape-controlled synthesis of metal nanocrystals. We begin with a brief introduction to nucleation and growth within the context of metal nanocrystal synthesis, followed by a discussion of the possible shapes that a metal nanocrystal might take under different conditions. We then focus on a variety of experimental parameters that have been explored to manipulate the nucleation and growth of metal nanocrystals in solution-phase syntheses in an effort to generate specific shapes. We then elaborate on these approaches by selecting examples in which there is already reasonable understanding for the observed shape control or at least the protocols have proven to be reproducible and controllable. Finally, we highlight a number of applications that have been enabled and/or enhanced by the shape-controlled synthesis of metal nanocrystals. We conclude this article with personal perspectives on the directions toward which future research in this field might take.

Shape‐Controlled Synthesis of Metal Nanocrystals: Simple Chemistry Meets Complex Physics?

The development of nanocrystals has been intensively pursued, not only for their fundamental scientific interest, but also for many technological applications. The synthesis of monodisperse nanocrystals (size variation <5%) is of key importance, because the properties of these nanocrystals depend strongly on their dimensions. For example, the colour sharpness of semiconductor nanocrystal-based optical devices is strongly dependent on the uniformity of the nanocrystals, and monodisperse magnetic nanocrystals are critical for the next-generation multi-terabit magnetic storage media. For these monodisperse nanocrystals to be used, an economical mass-production method needs to be developed. Unfortunately, however, in most syntheses reported so far, only sub-gram quantities of monodisperse nanocrystals were produced. Uniform-sized nanocrystals of CdSe (refs 10,11) and Au (refs 12,13) have been produced using colloidal chemical synthetic procedures. In addition, monodisperse magnetic nanocrystals such as Fe (refs 14,15), Co (refs 16-18), gamma-Fe(2)O(3) (refs 19,20), and Fe(3)O(4) (refs 21,22) have been synthesized by using various synthetic methods. Here, we report on the ultra-large-scale synthesis of monodisperse nanocrystals using inexpensive and non-toxic metal salts as reactants. We were able to synthesize as much as 40 g of monodisperse nanocrystals in a single reaction, without a size-sorting process. Moreover, the particle size could be controlled simply by varying the experimental conditions. The current synthetic procedure is very general and nanocrystals of many transition metal oxides were successfully synthesized using a very similar procedure.

/pdf/ultra-large-scale-syntheses-of-monodisperse-nanocrystals-5ato45sv4b.pdf

Ultra-large-scale syntheses of monodisperse nanocrystals.

Nickel nanoparticles of tunable shape have been synthesized in THF, in the presence of hexadecylamine (HDA) or trioctylphosphineoxide (TOPO), in mild conditions and characterized by HREM and SQUID measurements. The formation of nanorods is promoted by a high amine content in the reaction medium. In contrast to what is observed for TOPO-protected nickel particles, the saturation magnetization of HDA-capped nanoparticles is comparable to that of bulk nickel, which demonstrates that the coordination of an amine ligand does not alter the magnetic properties of nickel.

Synthesis and Magnetic Properties of Nickel Nanorods

Shape Control of Thermodynamically Stable Cobalt Nanorods through Organometallic Chemistry

The decomposition of the ruthenium precursor Ru(COD)(COT) (1, COD = 1,5-cyclooctadiene; COT = 1,3,5-cyclooctatriene) in mild conditions (room temperature, 1--3 bar H(2)) in THF leads, in the presence of a stabilizer (polymer or ligand), to nanoparticles of various sizes and shapes. In THF and in the presence of a polymer matrix (Ru/polymer = 5%), crystalline hcp particles of uniform mean size (1.1 nm) homogeneously dispersed in the polymer matrix and agglomerated hcp particles (1.7 nm) were respectively obtained in poly(vinylpyrrolidone) and cellulose acetate. The same reaction, carried out using various concentrations relative to ruthenium of alkylamines or alkylthiols as stabilizers (L = C(8)H(17)NH(2), C(12)H(25)NH(2), C(16)H(33)NH(2), C(8)H(17)SH, C(12)H(25)SH, or C(16)H(33)SH), leads to agglomerated particles (L = thiol) or particles dispersed in the solution (L = amine), both displaying a mean size near 2--3 nm and an hcp structure. In the case of amine ligands, the particles are generally elongated and display a tendency to form worm- or rodlike structures at high amine concentration. This phenomenon is attributed to a rapid amine ligand exchange at the surface of the particle as observed by (13)C NMR. In contrast, the particles stabilized by C(8)H(17)SH are not fluxional, but a catalytic transformation of thiols into disulfides has been observed which involves oxidative addition of thiols on the ruthenium surface. All colloids were characterized by microanalysis, infrared spectroscopy after CO adsorption, high-resolution electron microscopy, and wide-angle X-ray scattering.

Ligand-stabilized ruthenium nanoparticles: synthesis, organization, and dynamics.

The influence of size reduction on the magnetism of CoRh has been studied on a system of isolated nanometric spherical bimetallic ultrafine particles embedded in a polymer matrix. Pulsed fields up to 30 T were used in order to approach the magnetic saturation ( ${M}_{S}$). Particles with a mean diameter of 1.65 $(\ifmmode\pm\else\textpm\fi{}0.1)\mathrm{nm}$ display a value of $2.38{\ensuremath{\mu}}_{B}$ per CoRh unit strongly enhanced compared to values calculated or measured on a bulk alloy. These results were interpreted as the first evidence of the cooperative role of both alloying and size reduction to the enhancement of ${M}_{S}$ in this system associating a $3d$ FM metal with a $4d$ metal.

Magnetic enhancement in nanoscale CoRh particles.

The reaction of Pt(dba)2 with CO (1 atm) in toluene affords a brown precipitate which can be isolated and redissolved in CH2Cl2 to give a colloidal solution of fcc platinum particles with a large s...

Marie-José Casanove

Papers

Synthesis and Magnetic Properties of Nickel Nanorods

Shape Control of Thermodynamically Stable Cobalt Nanorods through Organometallic Chemistry

Ligand-stabilized ruthenium nanoparticles: synthesis, organization, and dynamics.

Magnetic enhancement in nanoscale CoRh particles.

Synthesis and Isolation of Cuboctahedral and Icosahedral Platinum Nanoparticles. Ligand-Dependent Structures