Gallium oxide (Ga2O3) is emerging as a viable candidate for certain classes of power electronics, solar blind UV photodetectors, solar cells, and sensors with capabilities beyond existing technologies due to its large bandgap. It is usually reported that there are five different polymorphs of Ga2O3, namely, the monoclinic (β-Ga2O3), rhombohedral (α), defective spinel (γ), cubic (δ), or orthorhombic (e) structures. Of these, the β-polymorph is the stable form under normal conditions and has been the most widely studied and utilized. Since melt growth techniques can be used to grow bulk crystals of β-GaO3, the cost of producing larger area, uniform substrates is potentially lower compared to the vapor growth techniques used to manufacture bulk crystals of GaN and SiC. The performance of technologically important high voltage rectifiers and enhancement-mode Metal-Oxide Field Effect Transistors benefit from the larger critical electric field of β-Ga2O3 relative to either SiC or GaN. However, the absence of clear demonstrations of p-type doping in Ga2O3, which may be a fundamental issue resulting from the band structure, makes it very difficult to simultaneously achieve low turn-on voltages and ultra-high breakdown. The purpose of this review is to summarize recent advances in the growth, processing, and device performance of the most widely studied polymorph, β-Ga2O3. The role of defects and impurities on the transport and optical properties of bulk, epitaxial, and nanostructures material, the difficulty in p-type doping, and the development of processing techniques like etching, contact formation, dielectrics for gate formation, and passivation are discussed. Areas where continued development is needed to fully exploit the properties of Ga2O3 are identified.

A review of Ga2O3 materials, processing, and devices

β-Ga2O3 bulk crystals were grown by the edge-defined film-fed growth (EFG) process and the floating zone process. Semiconductor substrates containing no twin boundaries with sizes up to 4 in. in diameter were fabricated. It was found that Si was the main residual impurity in the EFG-grown crystals and that the effective donor concentration (N d − N a) of unintentionally doped crystals was governed by the Si concentration. Intentional n-type doping was shown to be possible. An etch pit observation revealed that the dislocation density was on the order of 103 cm−3. N d − N a for the samples annealed in nitrogen ambient was almost the same as the Si concentration, while for the samples annealed in oxygen ambient, it was around 1 × 1017 cm−3 and independent of the Si concentration.

http://iopscience.iop.org/article/10.7567/JJAP.55.1202A2/pdf

High-quality β-Ga2O3 single crystals grown by edge-defined film-fed growth

The successful growth of 2-in. β-Ga2O3 crystals by the edge-defined, film fed growth (EFG) method was demonstrated. The optimization of growth conditions for larger single crystalline β-Ga2O3 is discussed in detail. The seeding conditions of temperature and neck width were found to be the most important factors to grow single crystals. X-ray rocking curve measurements of β-Ga2O3 crystals were conducted to estimate the dislocation densities of the grown crystals. Etch pit densities (EPDs) of the β-Ga2O3 crystals were also measured using KOH solution to measure the dislocation densities. The results were discussed combining with crystal growth parameters such as neck width to clarify the mechanisms of propagation and the origin of dislocations in crystals from phenomenological and crystallographic points of view.

https://iopscience.iop.org/article/10.1143/JJAP.47.8506/pdf

Growth of β-Ga2O3Single Crystals by the Edge-Defined, Film Fed Growth Method

On the bulk β-Ga2O3 single crystals grown by the Czochralski method

Ga2O3 thin films of the α-phase, that is, the corundum structure (in the trigonal system), have been epitaxially obtained on sapphire (α-Al2O3) substrates, in contrast to the strong tendency of Ga2O3 to assume a heterogeneous crystal structure, that is, the β-gallia structure (in the monoclinic system) on sapphire. This result is advantageous for high-quality films and is due to the growth by mist chemical vapor deposition (CVD) at low temperatures of 430–470 °C. The α-Ga2O3 films have narrow full-widths at half maximum (FWHMs) in their X-ray diffraction rocking curves, for example, about 60 arcsec. The root mean square (RMS) roughness of the surface was as small as 1 nm. The optical band gap energy obtained was 5.3 eV, and the films were almost completely transparent in the near-ultraviolet and visible regions. The epitaxial growth of α-Ga2O3 films on sapphire is beneficial for the fabrication of oxide optical and electronic devices.

https://iopscience.iop.org/article/10.1143/JJAP.47.7311/pdf

Heteroepitaxy of Corundum-Structured α-Ga2O3 Thin Films on α-Al2O3 Substrates by Ultrasonic Mist Chemical Vapor Deposition

Growth and spectral characterization of β-Ga2O3 single crystals

The crystallographic properties and defects of hydrothermally grown barium titanate crystallites are reported. When a precursor with a Ba:Ti molar ratio of 1.0 was used, cubic barium titanate crystallites were formed. However, when the precursor Ba:Ti molar ratio was 3.0, the product was tetragonal. The defect concentration (including OH defects and barium vacancies) was higher in cubic crystallites than in tetragonal crystallites. Because of the defects in the crystallites, the displacement of Ba2+ cations and the deformation of the Ti-O6 octahedrons was suppressed; thus, no phase transition from cubic to tetragonal occurred at the Curie point. When the defects were eliminated by thermal treatment, the normal crystallographic properties were obtained. A high reaction temperature and a high Ba:Ti molar ratio in the precursor were beneficial to limiting defect dormation in the crystallites; thus, tetragonal crystallites were obtained.

Crystallographic Properties of Hydrothermal Barium Titanate Crystallites

Growth and characterization of new transparent conductive oxides single crystals β-Ga2O3: Sn

Ultra-wide bandgap beta-gallium oxide (β-Ga2O3) has been attracting considerable attention as a promising semiconductor material for next-generation power electronics. It possesses excellent material properties such as a wide bandgap of 4.6–4.9 eV, a high breakdown electric field of 8 MV/cm, and exceptional Baliga’s figure of merit (BFOM), along with superior chemical and thermal stability. These features suggest its great potential for future applications in power and optoelectronic devices. However, the critical issue of contacts between metal and Ga2O3 limits the performance of β-Ga2O3 devices. In this work, we have reviewed the advances on contacts of β-Ga2O3 MOSFETs. For improving contact properties, four main approaches are summarized and analyzed in details, including pre-treatment, post-treatment, multilayer metal electrode, and introducing an interlayer. By comparison, the latter two methods are being studied intensively and more favorable than the pre-treatment which would inevitably generate uncontrollable damages. Finally, conclusions and future perspectives for improving Ohmic contacts further are presented.

/pdf/recent-advances-in-b-ga2o3-metal-contacts-3w1846k9dk.pdf

Changtai Xia

Papers

Growth and spectral characterization of β-Ga2O3 single crystals

Crystallographic Properties of Hydrothermal Barium Titanate Crystallites

Growth and characterization of new transparent conductive oxides single crystals β-Ga2O3: Sn

Recent Advances in β-Ga2O3-Metal Contacts.

Synthesis and magnetic properties of Ni-doped zinc oxide powders