Fundamentals and advances in magnesium alloy corrosion

X-ray computer tomography (CT) is fast becoming an accepted tool within the materials science community for the acquisition of 3D images. Here the authors review the current state of the art as CT transforms from a qualitative diagnostic tool to a quantitative one. Our review considers first the image acquisition process, including the use of iterative reconstruction strategies suited to specific segmentation tasks and emerging methods that provide more insight (e.g. fast and high resolution imaging, crystallite (grain) imaging) than conventional attenuation based tomography. Methods and shortcomings of CT are examined for the quantification of 3D volumetric data to extract key topological parameters such as phase fractions, phase contiguity, and damage levels as well as density variations. As a non-destructive technique, CT is an ideal means of following structural development over time via time lapse sequences of 3D images (sometimes called 3D movies or 4D imaging). This includes information nee...

https://www.tandfonline.com/doi/pdf/10.1179/1743280413Y.0000000023

Quantitative X-ray tomography

This review highlights recent advances in X-ray microcomputed tomography (microCT) as applied to materials, specifically advances made since the first materials microCT review appeared in Internati...

Recent advances in X-ray microtomography applied to materials

Numerical investigation on stress concentration of corrosion pit

Novel images of the evolution of stress corrosion cracks from corrosion pits

Two forms of high resolution X-ray tomographic experiments (i.e. synchrotron based X-ray microtomography and desktop microfocus computed X-ray tomography) are demonstrated in the present paper to illustrate the wide application of these techniques for qualitative and quantitative studies of localised corrosion and environmentally assisted cracking. Specifically, synchrotron based X-ray tomography was used to investigate the localised corrosion morphology within aluminium specimens when exposed in situ to a chloride environment while microfocus computed X-ray tomography was used to investigate the morphology and quantify the transition from localised corrosion to stress corrosion cracking in steel specimens exposed ex situ to a simulated corrosive condensate environment.

D. A. Horner

Papers

X-ray microtomography studies of localised corrosion and transitions to stress corrosion cracking

Challenges in modelling the evolution of stress corrosion cracks from pits