Showing papers by "Philip A. Parilla published in 2009"
TL;DR: In this paper, a simple and straightforward method was developed using solid state 13C NMR and subtraction of the spectrum of a standard amorphous cellulose to evaluate the crystallinity index of cellulose.
Abstract: The crystallinity index of cellulose is an important parameter to establish because of the effect this property has on the utilization of cellulose as a material and as a feedstock for biofuels production. However, it has been found that the crystallinity index varies significantly depending on the choice of instrument and data analysis technique applied to the measurement. We introduce in this study a simple and straightforward method to evaluate the crystallinity index of cellulose. This novel method was developed using solid state 13C NMR and subtraction of the spectrum of a standard amorphous cellulose. The crystallinity indexes of twelve different celluloses were measured and the values from this method were compared with the values obtained by other existing methods, including methods based on X-ray diffraction. An interesting observation was that the hydration of the celluloses increased their crystallinity indexes by about 5%, suggesting that addition of water increased cellulose order for all the cellulose samples studied.
225 citations
TL;DR: 3-D nanoengineered fibers physisorb twice as much hydrogen per unit surface area as do typical macroporous carbon materials and points a way toward solving the volumetric and heat-transfer constraints that limit some other hydrogen-storage supports.
Abstract: Single-walled carbon nanotube (SWCNT) fibers were engineered to become a scaffold for the storage of hydrogen. Carbon nanotube fibers were swollen in oleum (fuming sulfuric acid), and organic spacer groups were covalently linked between the nanotubes using diazonium functionalization chemistry to provide 3-dimensional (3-D) frameworks for the adsorption of hydrogen molecules. These 3-D nanoengineered fibers physisorb twice as much hydrogen per unit surface area as do typical macroporous carbon materials. These fiber-based systems can have high density, and combined with the outstanding thermal conductivity of carbon nanotubes, this points a way toward solving the volumetric and heat-transfer constraints that limit some other hydrogen-storage supports.
76 citations
TL;DR: In this article, the phase evolution of the binary (In-Se and Cu-Se) and ternary (Cu-InSe) MOD precursor films was examined during processing to evaluate the nature of the phase and composition changes.
Abstract: In2Se3, Cu2Se, and CuInSe2 thin films have been successfully fabricated using novel metal organic decomposition (MOD) precursors and atmospheric pressure-based deposition and processing. The phase evolution of the binary (In-Se and Cu-Se) and ternary (Cu-In-Se) MOD precursor films was examined during processing to evaluate the nature of the phase and composition changes. The In-Se binary precursor exhibits two specific phase regimes: (i) a cubic-InxSey phase at processing temperatures between 300 and 400 °C and (ii) the γ-In2Se3 phase for films annealed above 450 °C. Both phases exhibit a composition of 40 at.% indium and 60 at.% selenium. The binary Cu-Se precursor films show more diverse phase behavior, and within a narrow temperature processing range a number of Cu-Se phases, including CuSe2, CuSe, and Cu2Se, can be produced and stabilized. The ternary Cu-In-Se precursor can be used to produce relatively dense CuInSe2 films at temperatures between 300 and 500 °C. Layering the binary precursors together has provided an approach to producing CuInSe2 thin films; however, the morphology of the layered binary structure exhibits a significant degree of porosity. An alternative method of layering was explored where the Cu-Se binary was layered on top of an existing indium-gallium-selenide layer and processed. This method produced highly dense and large-grained (>3 µm) CuInSe2 thin films. This has significant potential as a manufacturable route to CIGS-based solar cells.
12 citations