About: National Institute of Technology, Karnataka is a education organization based out in Mangalore, Karnataka, India. It is known for research contribution in the topics: Computer science & Corrosion. The organization has 5017 authors who have published 7057 publications receiving 70367 citations.

Corrosion behavior of composition modulated multilayer Zn–Co electrodeposits produced using a single-bath technique

Abstract: Composition modulated alloy (CMA) electrodeposits of Zn–Co were produced from acid chloride baths by the single-bath technique. Their corrosion behavior was evaluated as a function of the switched cathode current densities and the number of layers. The process was optimized with respect to the highest corrosion resistance. Enhanced corrosion resistance was obtained when the outer layer was slightly richer with cobalt. At the optimum switched current densities 40/55 mA cm−2, a coating with 600 layers showed ~6 times higher corrosion resistance than monolithic Zn–Co electrodeposit having the same thickness. The CMA coating exhibited red rust only after 1,130 h in a salt-spray test. The increased corrosion resistance of the multilayer alloys was related to their inherent barrier properties, as revealed by Electrochemical Impedance Spectroscopy. The corrosion resistance was explained in terms of n-type semiconductor films at the interface as supported by Mott–Schottky plots.

Study of wear behaviour of austempered ductile iron

Abstract: An investigation was carried out to examine the influence of austempering temperature on microstructural parameters and the wear behaviour of austempered ductile iron. Ductile iron was austenitised at 900 °C for 30 min and austempered for 2 h at 260, 280, 300, 320, 350, 380 and 400 °C. Resulting microstructures were characterised through optical microscopy and X-ray diffraction. Wear test was carried out using a pin-on-disc machine with sliding speed of 289 m min−1. Coarse ausferrite microstructure exhibited higher wear rate than fine ausferrite microstructure. At high austempering temperature large amounts of austenite was instrumental in improving the wear resistance through formation of deformation induced martensite. Study of the wear surface under scanning electron microscope showed that, under dry sliding condition, wear occurred mainly due to adhesion and delamination. Wear rate was found to be dependent on the yield strength, austenite content and its carbon content.